Synthesis of magnesium oxide from waste magnesium-rich Cucurbita pepo (pumpkin) seeds

ABSTRACT Recent studies have focused on the processing of biowaste to obtain added value and to reduce organic waste in the general stream. This study investigated the synthesis of magnesium oxide (MgO) from magnesium-rich Cucurbita pepo (pumpkin) seeds for a precursor solution as a reducing agent via an eco-friendly method for the first time. The pumpkin seeds were ashed at 550°C for 6 h and subjected to acid-leaching. Mg(OH)2 was then precipitated using an aqueous solution of 2.0 M NaOH. The Mg(OH)2 was then calcined at 550°C for 4 h to obtain MgO. Physicochemical properties (i.e. proximate analysis, elemental composition, electrical conductivity (EC), pH) and selected heavy metals (i.e. Pb, Fe, As, Cd, Cr, Hg, Cu, and Ni) analyses were conducted on the seed samples and as-synthesized MgO. X-ray fluorescence (XRF), X-ray diffraction (XRD), Fourier-transform infrared (FTIR), citric acid test (CAT), and acid neutralization capacity (ANC) tests were techniques used to characterize the synthesized MgO. The results revealed the percentage yield of the MgO to be 23%. The pH of the as-synthesized MgO was recorded as 10.63. XRF studies showed that MgO made up 75.1% of the total weight synthesized. XRD results showed the presence of crystalline cubic structures of MgO. FTIR results showed a peak at 584 cm−1 which confirmed the formation of MgO. The produced MgO was highly reactive, with a CAT time of 2 s. The ANC of the MgO was high at 22.77 mol+/kg. Also, metal concentrations such as Fe, Cu, Cd, Ni, Pb, Hg, As, and Cr in MgO were below the WHO stipulated limits of 350, 36, 0.8, 35, 85, 0.03, 40, and 100, respectively. This implies its suitability for soil remediation purposes. Results indicate that the as-synthesized MgO from Cucurbita pepo (C. pepo) seeds could be used for several applications due to its high alkalinity, reactivity, and fast CAT time.


Introduction
The rise in the development of new technologies is creating opportunities for the use of new, innovative, and waste materials.These materials can be tailored to possess the right mix of microstructure and properties for innovative solutions to societal problems.Several materials including metal oxides have been reported in the literature to possess unique functionalities and applications in numerous fields (Dehghan et al., 2022;Kalita et al., 2021;Mohamed et al., 2021;THI Tran et al., 2021).One of these metals, magnesium (Mg) and its compounds, since early 2000 has found extensive application within the healthcare industry (DE Baaij et al., 2015;Safford et al., 2015;Witte, 2010).As a result, the use of Mg and its compounds has risen requiring an increase in its production (Hornak, 2021;Nagappa & Chandrappa, 2007).Magnesium oxide (MgO) is one of the most important inorganic oxides in waste and toxicity management (FOUDA et al., 2021).
MgO is notably obtained from their orebodies (magnesite, dolomite, brucite and olivine) (Shand, 2006) and seawater or brine (HØY-Petersen & Rizley, 2020;Zhang et al., 2021).There is, however, no universal access to these resources, as they tend to be concentrated only in some areas of the world (Daigle & DeCarlo, 2022).Whereas the orebodies are mainly concentrated in a few countries in Asia, Europe, North and South America (Wu et al., 2021), seawater/brine is not accessible to land-locked areas, hence other sources of MgO production are necessary to supplement the high demand of MgO being predicted.Again, research has shown that the low concentration of magnesium in seawater (~1.3 g/cm 3 ) gives rise to design problems during its synthesis (Kulekci, 2008;Song & Atrens, 1999).Also, the extraction of MgO from their raw materials has been reported to negatively influence their environment (HØY-Petersen & Rizley, 2020;Zhang et al., 2021).Furthermore, the synthesis of MgO from these two sources has not been able to generate the quantities needed worldwide (Sabouri et al., 2022).Therefore, researchers are finding alternate ways of increasing the production of Mg and its compound stocks from alternative raw materials to meet their ever-increasing demand (Jassim et al., 2020).The price of MgO has been souring on the global market due to demand surpassing supply of the MgO commodity (Nobre et al., 2020).Therefore, there is a high research drive in the production of MgO in order to make the product affordable and hence for its continuous use in low-end applications.Fernández (2022) has projected an annual production increase of 1.5% between the period of 2020 to 2029.A lot of research is currently ongoing to close the demand-supply gap and hence the increasing world prices.
Recently, a plant-mediated pathway for synthesizing metal oxide has received much attention due to their environmental benign when compared to conventional methods (Mesías et al., 2013;Mousavi et al., 2019;Yusufoğlu et al., 2020).Several plant-based sources of magnesium have been utilized for the synthesis of MgO.For instance, Tabrez et al. (2022) investigated the anticancer efficacy of biogenic synthesized MgONPs by using Cucurbita maxima pumpkin seeds by utilizing a filtered pumpkin seed extract obtained from reflux of powdered seeds in deionized water as their reducing agent.However, there are issues when it comes to their yield and the quality of the MgO produced.Therefore, there is a need to study alternative sources of magnesium for the synthesis of MgO.To the best of our knowledge, there is no study on the synthesis of MgO from Cucurbita pepo (pumpkin) seeds for a precursor solution as a reducing agent.
Cucurbita species (Pumpkins) are among the top 10 widely grown vegetables in the world (Rolnik & Olas, 2020).Among their wide varieties, Cucurbita pepo (Linn) has the most monetary value and is also the commonest Cucurbita species grown in Ghana (Abbiw, 1990;Glew et al., 2006).The flesh of pumpkins has been used for decades for food and medicinal purposes (Glew et al., 2006).Their seeds, however, have been viewed as waste and are dumped in landfills or as animal feed.With the advent of nutritional composition studies, C. pepo seeds have been discovered to be rich in nutrients, particularly magnesium (Badu et al., 2020;Kwiri, 2014).Since then, there has been a rise in the consumption of these seeds in food and medicine (Devi et al., 2018;Glew et al., 2006).Consumption, however, in Ghana and several other African countries is still significantly low, with the seeds still mainly treated as waste (Badu et al., 2020).In meeting the UN Sustainable Development Goals (SDG12 Responsible consumption and production), instead of discarding as waste, the Mgrich C. pepo seeds can serve as a unique source of MgO for various practical applications.This study, therefore, seeks to investigate the extraction and synthesis of MgO from Cucurbita pepo (pumpkin) seeds.

Methods
De-hulled C. pepo seeds were obtained from a seed shop in Techiman, a town in the Bono-East Region of Ghana.Sodium hydroxide (NaOH) pellets and hydrochloric acid (HCl) (70%w/v) used in this study were purchased from VWR Chemicals (France).De-ionized water was used throughout the experiment.

Preparation of magnesium precursor
Seed preparation was done using the approach adopted by Bitog et al. (2009).The fresh seeds were first weighed on a Sartonous BP 6100 model electronic mass balance as initial weight (W 1 ).They were then cleaned and dried in an oven at 105°C for 24 h.The final weight (W 2 ) was recorded.The seeds were then ground in a porcelain mortar and pestle.A portion of the ground seed samples was taken for physicochemical analysis, and the rest were ashed in a Nabertherm muffle furnace at 550°C for 6 h.The resultant ash was weighed and stored in airtight bags for further processing and analysis.
The process by which the magnesium precursor was prepared was adapted from Royani et al. (2018).The pumpkin seed ash samples were washed with de-ionized water in a hot water bath at 60°C for 2 h.The solution was then filtered with a Whatman No. 1 filter paper, and the residue (seed ash) was dried at 105°C for 3 h.Thereafter, the dried seed ash was added to 2.0 M HCl at a liquid-to-solid ratio of 20 ml/g, with constant stirring at 400 rpm at 75°C for 3 h.The mixture was then filtered with a Whatman No.1 paper afterwards, and the filtrate, which is the magnesium precursor was stored for the magnesium oxide (MgO) synthesis.

Synthesis of magnesium oxide
A 2.0 M NaOH solution was prepared by dissolving NaOH pellets in distilled water.A total of 1.0 L of the solution was prepared.The process of synthesis was adapted from Daisy et al. (2015).The prepared Mg precursor solution (i.e. the leached ash from the C. pepo seeds) was added to the NaOH solution in a volume ratio of 1:1.After the formation of a white precipitate (Mg(OH) 2 ), the solution was heated at 100°C for 1 h.Afterwards, the solution was cooled and the Mg(OH) 2 was observed to settle at the bottom.The solution was filtered with a Whatman No. 1 filter paper and the precipitate was washed with de-ionized water several times until all water-soluble compounds had been removed.The washed Mg(OH) 2 precipitate was then dried and calcined in a muffle furnace at 550°C for 4 h to obtain the MgO.The MgO was transferred into a tight-lid vial and stored in a desiccator for further analysis.The yield of the synthesized MgO was calculated as:

Characterization of C. pepo seeds
Proximate composition (moisture and ash content, volatile matter, fixed carbon) was conducted according to García et al. (2013).The macro elements (phosphorus, magnesium, calcium, sodium, and potassium) of the Cucurbita pepo seeds were determined according to the method proposed by Rafiu (2012).Nitrogen (N) content was determined by the Kjeldahl method (Rafiu, 2012).Sulfur (S) content was determined by the turbidimetric method (Motsara & Roy, 2008).Walkley-Black wet oxidation method was used to determine Organic carbon (C) (Nelson & Sommers, 1983).The exchangeable acidity titrimetric method according to Mclean (1965) was used to determine the hydrogen (H) content.Oxygen was calculated as %Oxygen Heavy metals (Pb, Fe, As, Cd, Cr, Hg, Cu, and Ni) in the C. pepo seeds were analyzed by an atomic absorption spectrophotometer (AAS), using a tri-acid mixture (HClO 4 -HNO 3 -HCl) in a volume ratio of 1:2:3 (Kimbrough & Wakakuwa, 1989).

Characterization of the As-synthesized MgO
X-ray fluorescence (XRF) analysis was conducted on the powdered MgO sample using a Philips PW2400 X-ray sequential spectrophotometer to determine their elemental constituents.X-ray diffraction (XRD) analysis on the MgO was conducted using a PAN analytical Empyrean Series machine.The analysis was carried out with CuKα radiations at 45 kV and 40 mA 2θ range scanned from 5° to 99°, step 0.1050, and a counting time of 47 s.The mineral phase was identified using the X'Pert Highscore software package.Fourier-transform infrared (FTIR) analysis was performed in the range of 4000-400 cm −1 to detect and analyze the functional groups present in the MgO particles by an FTIR Spectrometer (Amina et al., 2020).The average crystallite size of MgO was determined using the Debye-Scherrer formula (Dobrucka, 2016).

D ¼ Kλ βcosθ
Eq:2 where D is the nanoparticle crystalline size, K denotes the Scherrer constant (0.98), λ represents the wavelength, and β is the full width at half maximum.
Citric acid test (CAT) was conducted according to Strydom et al. (2005) to determine the reactivity of the produced MgO.The test measures the time it will take for MgO to neutralize an acid, by causing a change in the pH of a solution to 9 (de Valle-Zermeño et al., 2015).The test was done by adding phenolphthalein drop by drop into a 1:50 solution of MgO and 0.40 N citric acid solution.A color change from white to pink (at pH = 9) indicates the completion of the reaction (Strydom et al., 2005).ANC test was conducted according to DEL Valle-Zermeño et al. (2015).
Acid neutralization capacity (ANC) evaluates the ability of the synthesized MgO particles to provide a buffer pH range which ensures minimum solubility of acids over a period (DEL Valle-Zermeño et al., 2015).This was done by determining the volume of acid (1.0 M HNO 3 , 65 wt%) that was needed to drop the pH of the MgO solution from that of minimum solubility (pH ≥ 9) to pH that allows metal redissolution (pH ≤ 4).
Heavy metal concentrations of the produced MgO were determined according to EPA Method 3050 B (SW-846).The analysis was done by digesting 1 g of MgO with a tri-acid mixture (HClO 4 , HNO 3 , and HCl) in a 1:2:3 ratio.The concentrations of (Fe, Pb, Cu, Cd, Ni, Cr, Hg, and As) were analyzed by an atomic absorption spectrophotometer (SPECTRA AA 220 Airacetylene Flame)

Proximate and elemental composition of C. pepo seeds
The average moisture content (%MC) recorded for the C. pepo seeds was 5.63 ± 0.06% as shown in Table 1.Similar values were recorded by Kwiri (2014) and STEINER-ASIEDU et al. (2014), with a slightly higher value recorded by Badu et al. (2020).Bowman and Barringer (2012) reported that the %MC of C. pepo seeds can be as high as 50%.Given the comparatively lower %MC in this study, it can be implied that the C. pepo seeds were dry.Generally, ash content of biomass is reported in published studies to be low (Zając et al., 2018), and in this study, C. pepo seeds produced low quantities of ash (4.31 ± 0.29%).The obtained value was similar to STEINER-ASIEDU et al. (2014) and Badu et al. (2020), but higher than Kwiri (2014).
The average volatile matter (%VM) of the seeds was recorded as 93.46 ± 0.99%.C. pepo seeds have notably high volatile matter content (>70%) as recorded by literature, due to high levels of fatty acids and oil (Bowman & Barringer, 2012;Zając et al., 2018).Bowman and Barringer (2012) also reported that a low %MC in the seeds resulted in higher %VM and vice versa, which was confirmed in this study.The average fixed carbon content (%FC), which determines the biochar left after combustion, was recorded at 2.22 ± 1.28% in conformance with Zając et al. (2018).%FC is also dependent on the %VM, as a high %VM is indicative of a low %FC, as observed in this study.
The elemental composition of the ashed-seed is presented in Table 2. Average Carbon (C) content was high as 50.21 ± 0.90%.This is similar to Bitog et al. (2009) who noted that biomass has high C content.Relatively lower values of Hydrogen (H) and Nitrogen (N) were recorded in this study.This is because H content vaporizes in combustion and the N content does not combust in temperatures less than 1000°C (Bitog et al., 2009).Sulfur (S) content was expectedly low and was recorded as 0.07 ± 0.01%.
C. pepo seeds are notably rich in various minerals.Constituent major minerals for this study are presented in Table 3. Mineral concentration was in the increasing order of sodium < magnesium < calcium < potassium < phosphorus.The results obtained were consistent with Sinkovič et al. (2021) who also recorded higher concentrations of phosphorus (1125 mg/100 g) and potassium (860 mg/100 g).Several other works also recorded higher concentrations of P and K (Glew et al., 2006;Kwiri, 2014;Rezig et al., 2019;Seymen et al., 2016).
Magnesium content (250 mg/100 g) recorded in this study was within the range reported by Seymen et al. (2016) (127.52-393.82mg/100 g).The recorded value was higher than that of Elinge et al. (2012) GARCIA et al., 2004;Shen et al., 2019).This value confirms MgO as a strong basic oxide that can be effective for purposes like soil remediation due to its high alkalinity.EC of the MgO was relatively high (2930 ± 26.46 µS/cm), signifying the presence of many mobile inorganic ions.Miller and Curtin (2006) noted that the conductivity of a solution is dependent on the concentration of all the constituent ions and the types of those ions.They noted that higher ion concentrations, particularly inorganic, resulted in a higher conductivity value.Inorganic ions such as Na + , K + , Mg 2+ , Ca 2+ , HCO 3-, Cl − , and SO 4 2-are strong electrolytes, due to the ease of complete dissociation.Thus, the synthesized MgO particles may contain a high concentration of these ions, thus its high EC value.The temperature of MgO was recorded at 27.77 ± 0.86°C.Temperature is relevant for the movement of ions in a medium and facilitates chemical reactions (Onwuka & Mang, 2018).This is an essential property for works concerning stabilization and photocatalysis.Sulphate concentration (mg/L) was recorded as low as 0.014 ± 0.00.

Presence of functional groups in the synthesized MgO
In this study, the FTIR profile of MgO displayed five main bands assigned to different functional groups (Figure 1(a)).The broad band at 3461 cm −1 represents the stretching frequency of the O-H bond (3500-3200 cm −1 ), which is due to the formation of an alcoholic compound along with MgO in synthesis (Jeevanandam et al., 2017).This bond may also represent residual water molecules from the reducing agent solution for synthesis (Ashok et al., 2016;Kandiban et al., 2015).The band around 1600 cm −1 according to Ashok et al. (2016) represents an endothermic peak due to the weak stretching vibration of water molecules.In this study, however, this peak could represent the N-H bend (primary amine), due to the presence of the amino acid Lysine, which is present in C. pepo seeds (Devi et al., 2018;Jeevanandam et al., 2017).
The band around 1400 cm −1 is representative of O-H bending vibration according to (Amina et al., 2020).C=O stretching frequency is observed at the broadband at 1381 cm −1 which denotes the presence of an aromatic ring (Kandiban et al., 2015).The peak at 584 cm −1 in the range of 660-540 cm −1 represents Mg-O stretching, which signifies the formation of MgO (Amina et al., 2020;Ashok et al., 2016;Jeevanandam et al., 2017;Kandiban et al., 2015).
The major mineralogical phases in the MgO powder were identified by XRD analysis in Figure 1(b).In Figure 1(b), the major phases present are MgO and NaCl.This result confirms the high EC value obtained   for the particles (Section 3.2.2) which implied a high concentration of mobile ions such as Mg 2+ , Na + , O 2-, and Cl − .The synthesized MgO particles are of a cubic structure and crystalline nature.MgO was present in its crystalline form Periclase, with diffraction peaks at 36.78°, 42.88°, 62.24°, 74.98°, 78.83°, and 93.10°.These peaks are representative of the ( 111), ( 200), ( 220), ( 311), ( 222), and (400) crystal planes, respectively.These planes are characteristic of MgO as recorded by several studies (Amina et al., 2020;Camtakan et al., 2012;Jhansi et al., 2017;Mantilaka et al., 2014).Identified peaks were almost similar to that obtained by Jhansi et al. (2017) and Balakrishnan et al. (2020).From Figure 1(b), it is observed that the highest intensity peak is obtained at 42.88°, representing the (200) planes of MgO, consistent with MgO diffraction analysis in literature.
The average crystallite size was determined from the most intense peak (42.88°) using the Debye-Scherrer equation as 26 nm.Camtakan et al. (2012) recorded a close value of 24 nm when they synthesized MgO using MgCl 2 and NaOH.The value was also nearly similar to that of Krishnamoorthy et al. (2012) (25-27 nm) who synthesized MgO using neem leaves.Amina et al. ( 2020) recorded higher crystallite sizes of 30 nm and 34 nm in their study using Indian Wood Costus and Sea Incense Costus.Lesser sizes were, however, recorded by Jhansi et al. (2017) (15-20 nm) and Dobrucka (2016) (10 nm).
Generally, crystallite size is inversely proportional to peak width-FWHM (β) (Speakman, 2014).This was confirmed by increasing crystallite size with decreasing β values obtained from the XRD spectrum data, as well as the narrow peaks observed in Figure 1(b).Crystallite size also increases by increasing calcination temperature (Krishnamoorthy et al., 2012;Pilarska et al., 2017;Tang & LV, 2014).The authors noted that calcination temperature above 800°C increased crystallite size.Calcination temperature employed in this study was lower (500°C), hence the smaller crystallite size.
Sodium Chloride (NaCl) was present as Halite and was identified in the synthesized particles as impurities.The constituent NaCl may have been produced from the reaction between the NaOH used as the reducing agent and the HCl used as the leaching medium of the seed ash.NaCl content can be reduced by extended washing of Mg(OH) 2 precipitate before calcination.

Reactivity of the synthesized MgO
In this study, the time for color change at pH 9 was recorded as 2 seconds (s).The obtained reactivity (s) value was categorized as highly reactive according to Strydom et al. (2005).The reactivity time obtained implies that the produced MgO can raise the pH of a system to 9, where acid is neutralized at a fast rate.In practice, this quality is highly desirable in areas such as heavy metal stabilization, where there is a need for a shorter remediation time.The value recorded was significantly lower than DEL Valle-Zermeño et al. ( 2015) who recorded >810 s for LG-MgO, Shen et al. (2019) at 33-3322 s, and GIRO-Paloma et al. ( 2020) at 60-1320 s.Reactivity also informs about the specific surface area of the MgO, and the higher the reactivity, the greater the surface area.Reactivity is also dependent on calcination temperatures for MgO.The higher the calcination temperature, the lower the surface area and the lower the reactivity (GIRO-Paloma et al., 2020;Shen et al., 2019).In this study, calcination was done at a low temperature of 500°C, hence the high reactivity of the MgO.

Acid neutralization capacity of the synthesized MgO
The results of the ANC of the MgO, which is presented as a curve of pH against hydronium (H 3 O + ) per mass of solid are shown in Figure 2. From Figure 2, three phases of the ANC curve and equilibrium were established.The first phase was observed in a pH range between 11.1 and 10.05 and the second phase was marked by a pH between 10.05 and 8 over a wide range of acid additions.The last phase was observed from pH 8 to 4. It is noteworthy that some alkali species present in the MgO establish a solubility equilibrium when they come into contact with water, and form their corresponding hydroxides.The composition of oxide is crucial to and affects the ANC curve results.This is because the hydroxides of metals are that which are involved in solubility control reactions (GIRO-Paloma et al., 2020).
The pH of the synthesized powder started from 11.1, which is higher than the natural pH of MgO (<11).This is due to the presence of CaO in the particles as shown in Table 2, whose hydroxide (Ca(OH) 2 ) controlled the solubility of the first phase.A drop in pH caused by an addition of a small amount of nitric acid (mol H 3 O + ) brought the pH to 10.05, at which stage solubility is controlled by the hydration product of MgO (Mg(OH) 2 /brucite).The takeover of solubility from Ca(OH) 2 by Mg(OH) 2 was fast due to the high reactivity of the produced MgO.There is also the possibility that added acid (HNO 3 ) quickly consumed the CaO in the first stage (GIRO-Paloma et al., 2020).
From pH of 10.05, the second phase was exclusively controlled by the solubility equilibrium of Mg(OH) 2 , which acted as a buffering agent over a long range of acid (HNO 3 ) additions as shown in Figure 2. DEL Valle-Zermeño et al. (2015) noted that hydration reactions easily reach equilibrium and slow down neutralizing reaction rates.It can be observed that acid consumption of the MgO was considerably high, especially in the range between the natural pH (10.5) and pH 8, at which point a gradual drop was observed, with a similar observation noted by DEL Valle-Zermeño et al. (2015) and GIRO-Paloma et al. (2020).
The third phase of the ANC results was marked by a descending curve in the pH 8-4 range.As pH fell below 8, solubility became more prominent and may have resulted from the dissolution of some metal hydroxides such as Zn(OH) 2 .Low pH at this phase may have also been controlled by the solubility of H 3 PO 4 which was present in the oxide powder.It is worth noting that the Al 2 O 3 , SiO 2 , and Fe 2 O 3 present in the MgO particles did not influence the ANC curve since they remain inert in their precipitated forms (GARCIA et al., 2004;GIRO-Paloma et al., 2020).
It can be inferred from the foregoing, that MgO provides a buffer at a pH range of 8-10.05,where it can resist pH changes for consecutive acid additions till pH drops.ANC required to exceed minimum solubility (pH 8.5-10.5)was 15.78 mol + /kg.To further lower the pH to 4, where redissolution of acids may occur, ANC required was high at 22.77 mol + /kg.GIRO-Paloma et al. (2020) recorded ANC values of 16-25 mol + /kg in their comparative studies of low-grade MgO.Upper limits of ANC values are set at ≥20 mol + /kg (Ayensu et al., 2020;Wahlström et al., 2009).In this regard, the produced MgO had a high neutralizing capacity and can provide a stable pH range of minimum solubility over a long time against acidification.

Heavy metal concentrations in the synthesized MgO
The concentration of selected heavy metals analyzed in this study is presented in Table 5.The values obtained were very low, compared to standard limits set by WHO (1996).It can thus be implied that the concentrations are not high enough to confer significant degrees of toxicity when utilized for further purposes such as soil stabilization and toxic metal adsorption.The synthesized powder can thus be employed in areas such as contaminated soil and wastewater remediation.

Chemical composition of the synthesized MgO particles
The chemical composition of the synthesized MgO is presented in Table 6.From the table, the produced MgO powder contained magnesium oxide (MgO) as the most dominant oxide at 75.1%.This confirms the formation and successful synthesis of MgO from C. pepo seeds.) recorded in Section 3.2.2(Seshadri et al., 2016).There were observable differences in the concentrations of the elements and oxides such as Fe 2 O 3 and CuO analyzed by AAS and XRF.This may be due to the inert and precipitated states some oxides assume in alkaline conditions (GARCIA et al., 2004;Wahlström et al., 2009), in which regard their concentrations are not observably high.

Conclusion
This study investigated the production of magnesium oxide (MgO) from Cucurbita pepo seeds, as a way of obtaining value from bio-waste, and presenting an economical and environmentally safe MgO for environmental remediation applications.The sample seeds and synthesized MgO were deeply characterized by physicochemical and microscopic analytical methods.The obtained results revealed that the seeds had low quantities of moisture and ash but were high in volatile matter content.The seeds also contained significant quantities of mineral elements, with an Mg concentration of 250 mg/100 g.FTIR analysis confirmed the formation of MgO by the characteristic peak formation in the range of 660-540 cm −1 .XRF analysis revealed the MgO powder contained 75.1% of MgO out of the total weight.The particles were crystalline with a cubic structure and an average size of 26 nm.The synthesized MgO had a high pH, thus high alkalinity.It was also highly reactive with a reaction time of 2 s and had an ANC value of 22.77 mol + /kg, hence a high buffering capacity.Heavy metal analyses also showed that all the metal concentrations in the produced MgO were significantly lower than the WHO limits.Thus, the synthesis of MgO from C. pepo seeds was successful and can be used for further waste remediation studies.

Table 1 .
Average proximate composition of C. pepo seeds Values are expressed as Mean ± standard error of the mean

Table 2 .
Average elemental composition of C. pepo seeds

Table 3 .
Major minerals in C. pepo seeds

Table 4 .
Physicochemical properties of synthesized MgO

Table 6 .
Chemical composition of synthesized MgO