Effect of in-situ synthesized TiB2 on microstructure and mechanical property of Al/TiB2-SiC interpenetrating phase composites

ABSTRACT Al/TiB2-SiC composites were prepared based on TiB2-SiC porous ceramic preforms. The advantages of this work were characterized by the in-situ synthesized TiB2 in porous ceramic preforms which directly formed interconnected pores as well as TiB2-SiC ceramic skeletons during the one-step ceramic sintering. By controlling in-situ synthesized TiB2 volume fraction, it is possible to tailor TiB2-SiC preform structures so as to determine the structures and mechanical properties of Al/TiB2-SiC composites. The porous ceramic preforms with 20 vol% TiB2 addition achieved the highest porosity, the biggest pore size, but the lowest flexural strength. Al/TiB2-SiC composite with 20 vol% TiB2 addition showed the optimum mechanical properties. The improvement of mechanical properties of Al/TiB2-SiC composites was mainly ascribed to TiB2 additions as well as dense composite structures which were fully infiltrated with Al. This special interpenetrating structural feature and TiB2 addition also constituted an improved toughness through complex crack patterns such as branching, bridging, and deflection.

Many reports were conducted on Al/SiC IPCs because of the high wear resistance and superior high temperature mechanical properties of SiC ceramics [7,14,15]. Kota et al. [16] focused on the effect of SiC foam pore size on the strength of Al/SiC IPCs and concluded that IPCs with finer pore size obtained higher hardness. Xie et al. [7] emphasized the contribution of ductile Al phase and SiC-Al phase interface on the enhancement of toughness of Al/SiC IPCs. Wang et al. [17] paid attention to Young's modulus and internal friction of Al/SiC IPCs. And good interface bonding was obtained by applying glass bonding to fabricate SiC porous preforms at 850°C utilizing pulse electric current sintering. The effect of multimodal SiC particle distributions on SiC preforms was researched by Wang et al. [13] for the fabrication of Al/SiC IPCs by pressure-less infiltration. It was reported that a number of fine-size SiC particle agglomeration reduced its strength and thermal conductive [18]. For all the above strategies of IPCs fabrication, researchers focused on obtaining SiC porous preforms with fine and homogeneous microstructures to improve the mechanical properties of as-prepared IPCs.
TiB 2 addition to SiC matrix had already been proved the effective improvement in hardness, strength, toughness, and electrical conductivity [19][20][21][22] compared with pure SiC preforms. Moreover, introducing in-situ synthesized TiB 2 into SiC preforms also improved the wettability [23,24] with melted Al so as to obtain dense Al/TiB 2 -SiC composite with more excellent properties [25]. Moreover, cast A356 aluminum alloy were selected due to its remarkable weldability, pourability and fluidity as to make the Al/TiB 2 -SiC composites after infiltration with less flaws [23]. Thus, in the present study, we first prepared TiB 2 -SiC porous preforms based on in-situ reaction process and obtained Al/TiB 2 -SiC composites by A356 Al alloy infiltration. The effect of in-situ synthesized TiB 2 contents on the microstructures and mechanical properties of both the TiB 2 -SiC porous preforms and the Al/TiB 2 -SiC composites was investigated.
First, carbothermal reduction of TiO 2 which applied sucrose as a natural carbon source according to the following equation:

Characterization
The density and open porosity of Al/TiB 2 -SiC composites were measured by Archimedes' water-immersion method with deionized water as the medium. Phase identification of raw powders, porous TiB 2 -SiC preform and Al/TiB 2 -SiC composites were performed by X-ray diffraction method (XRD, SmartLab 9 kW, Rigaku, Japan) using Cu lamp (λ = 1.54056 Å). Mercury intrusion porosimeter (MIP, AutoPore IV 9500, Micromeritics Instrument Corp., USA) was applied to evaluate pore characteristics of porous preforms. The microstructures of porous preforms and composites were observed by scanning electron microscopy (SEM, JSM-7001F, JEOL, Japan). Elemental concentration profiles and phase distributions were measured using energy-dispersive spectroscopy (EDS where K IC is fracture toughness, P is the maximum load, L is bend span of 20 mm, b is the specimen width, W is specimen height, and a is the notch depth. At least three specimens were tested to get the average fracture toughness value.

TiB 2 -SiC preform
The pore morphologies and pore structural parameters of in-situ fabricated TiB 2 -SiC preforms were crucial for understanding the mechanical properties of both TiB 2 -SiC preforms and Al/TiB 2 -SiC composites. Figures 1(a, b, d, e, g, h, j, k) illustrated the morphologies of 15%, 20%, 25%, and 30% TiB 2 -SiC porous preforms in secondary electron (SE) and backscattered electron (BSE) imaging mode, respectively. The corresponding differential pore volume distributions as a function of the pore diameter on a logarithmic scale were plotted in Figures 1(c, f, i, l), respectively. MIP measurements were used to determine pore size distribution (PSD) curves. Porous preforms exhibited three-dimensional skeletons with highly interconnected pores. Bright-gray particles were in-situ formed TiB 2 particles in micro-and sub-micrometer scales with inherently random distribution. Some fine-size TiB 2 particles connected the bigger dark-gray SiC grains. Meanwhile, SiC sintering necks formed between SiC-SiC particles. Increasing amount of TiB 2 provided suppression on grain growth of SiC [26] which resulted in the decrease of ceramic grain size. Especially for 30% TiB 2 -SiC preform (Figure 1(g)), SiC grain size decreased compared with the other TiB 2 -SiC preforms [27]. Consequently, in-situ formed TiB 2 had due effects on pores formation and SiC grain interfacial bonding. Additionally, more direct TiB 2 -TiB 2 particle interactions were easily observed in 30% TiB 2 -SiC preform fracture morphologies. TiB 2 -TiB 2 particle interactions consequently resulted in highly heterogeneous pore distribution verified by the following MIP results.
As depicted in Figure 1(c), the pore volume distribution showed a pure and sharp peak for 15% TiB 2 -SiC preforms with the pore diameter in the range of 0.5-2 μm. The relatively narrow peak suggested an apparently uniform and interconnected pores. 20% TiB 2 -SiC preform exhibited the peak pore volume value at the pore diameter value of 2.06 μm with pore diameter ranging approximately from 1 μm to 4 μm, which was shown in Figure 1 (g). The pore sizes of both 15% and 20% TiB 2 -SiC preforms presented unimodal distributions. Pore size range increased continuously with TiB 2 content increasing. 25% TiB 2 -SiC preform showed the tendency of extending pore diameter range to a maximum value around 10 μm which was presented in Figure 1(i). Compared with the other TiB 2 -SiC preforms, 30% TiB 2 -SiC preform presented typical bimodal distributions with two clearly separated maxima as shown in Figure 1(l). 30% TiB 2 -SiC preform possessed a broad pore diameter range with the bigger pore diameter ranging from 2 µm to 15 µm, and the smaller pore diameter ranging from 0.5 µm to 2 µm. In 30% TiB 2 -SiC preform, pure TiB 2 -TiB 2 particle interactions left a number of the small-size pores. More TiB 2 particles attached to the porous skeleton also reduced the pore sizes. Porosities and flexural strength of TiB 2 -SiC preform were plotted in Figure 2 as a function of TiB 2 content. For four TiB 2 -SiC porous preforms, an overall porosity ranging from 36.2% to 41.9% was presented. 20% TiB 2 -SiC preform had the highest porosity. It was therefore possible to deduce that different TiB 2 contents effectively changed the pore structure and porosity.
The flexural strength presented the minimum value at 20% TiB 2 -SiC preform and then increased obviously with increasing TiB 2 volume fractions. For porous ceramic, Rice [28] described porosity-strength relationship which was closely approximated by an exponential equation given as: where σ is the strength at porosity P; σ 0 is the strength of a dense ceramic at zero porosity; b is an empirical constant. Increment in either porosity (P) led to degradation in global porous ceramic strength. For 20% TiB 2 -SiC preform, the highest porosity resulted in the lowest flexural strength which could be explained by Eq. (3). However, other porous preforms did not follow the strength-porosity relationship in Eq. (3). TiB 2 -SiC porous ceramic could be divided into three volumetric components: TiB 2 , SiC and pores. For the reason that TiB 2 exhibited higher Young's modulus and theoretical strength [22,29,30] than SiC, an increase in V TiB 2 was assumed to obtain higher strength. As a consequence, the increasing TiB 2 determined the improvement of the flexural strength of the 25% and 30% TiB 2 -SiC preforms. This clearly verified the strengthening effect of TiB 2 in ceramic preforms. When nearly all the pores were infiltrated with Al, it was assumed that increasing TiB 2 would result in the strength increasing of composites which would be discussed next.
The in-situ formed porous TiB 2 -SiC preform expressed a narrow and fine PSD providing a homogeneous porous structure which was responsible for affecting the properties of the Al/TiB 2 -SiC composites. By controlling the relative amount of the two ceramic phases, the permeability of the Al alloy infiltration [31] and different properties of final Al/TiB 2 -SiC composites would be studied next. Figure 3 schematically depicted the possible microstructural evolution of porous TiB 2 -SiC preform. The pores in TiB 2 -SiC preforms mainly resulted from initial residual porosity of loose-pack powders [32], burnout of C 12 H 22 O 11 , volume loss of starting powders, CO gas release [33], and grain-growth during final sintering. The in-situ reactive sintering process could be roughly divided into four stages as shown in Figure 3. Prior to sintering, the microstructure of loose-pack powders with obvious initiating pores in the green compacts was shown in Figure 3 (a). The porosity was partly attributed to the low density of green compacts. Figure 3(b) illustrated the decomposition of sucrose at the temperature range from 500°C to 550°C which formed according to the following reaction [34]: Pores were partly produced from volume loss of C 12 H 22 O 11 carbonization. After sucrose carbonization, pyrolysis carbon in small size completely transformed everywhere on all the loose-packed powders. It was well recognized that the high diffusion coefficient of free pyrolysis carbon residue [35,36] made it possible for the homogeneousness of the in-situ reaction to form TiB 2 . Rising temperature to 1400°C, carbothermal conversion (Eq. (1)) of TiO 2 started with the help of B 4 C and C as depicted in Figure 3(c). The migration of the starting reactants [37,38] significantly influenced the porous microstructure and increased the porosity. During the carbothermal reduction process, the oxygen extracted from TiO 2 was presented in the form of by-product gas CO. The expulsion of CO among the ceramic grains resulted in the generation of more pores [39], particularly open pores. Volume loss of the starting reactants and CO emission during the in-situ reactive sintering made the major contribution to porosity in the porous preforms.
Generally, further ceramic grain neck growth increased at the final sintering temperature of 1950°C. Sintering and coarsening of ceramic grains mainly conducted as depicted in Figure 3(d). SiC grains were sintered together with the newly insitu created TiB 2 simultaneously. On the other hand, the addition of TiB 2 was supposed to suppress exaggerated grain growth [40] of SiC. Thereby, more TiB 2 addition decreased the average size of ceramic particles, which was also verified by the different ceramic skeleton morphologies in Figure 1.

Phase composition, porosity and density of composites
In order to identify the in-situ reaction process and the phase constituents in the Al/TiB 2 -SiC composites, the XRD results of mixed starting powders, 20% TiB 2 -SiC preform before Al infiltration, and 20% Al/TiB 2 -SiC  composite after Al infiltration were characterized in Figure 4. According to Figure 4(a), the existence of all starting powders including TiO 2 , B 4 C, C and SiC was validated. After in-situ reactive sintering, the reaction product of TiB 2 was detected which was shown in Figure 4(b). Meanwhile, only TiB 2 and SiC diffraction were identified in 20% TiB 2 -SiC preform without other starting powders. In this regard, TiB 2 was successfully synthesized as a result of completed carbothermal reduction between TiO 2 , B 4 C, and C. After Al infiltration, the peaks of SiC, TiB 2 and Al phases were mainly characterized in the Al/TiB 2 -SiC composite, andatrace amount of Si was also detected in Figure 4(c). The detected Si was from A356 Al alloy which was a typical commercial Al-Si alloy containing approximate 7 wt.% Si [23]. Moreover, harmful interfacial reaction product Al 4 C 3 [1,41,42] as one of the major concerns in SiC/Al composite was not detected in the Al/TiB 2 -SiC composite from the XRD results. Figure 5 recorded density and porosity of Al/TiB 2 -SiC composites as a function of TiB 2 volume fraction. Volume density decreased and the porosity increased distinctly with the increase in the amount of TiB 2 volume fraction. 15% Al/TiB 2 -SiC composites had optimum porosity of 0.54%. The porosity value of 20% Al/TiB 2 -SiC composites increased slightly. However, with a further increase in TiB 2 volume fraction, the porosity increased significantly. Opening porosity increased to 3.26% for 30% Al/TiB 2 -SiC composite. Considering the PSD of 30% TiB 2 -SiC preform obtained from MIP and the microstructure morphologies, it was deduced that some small size pores in 30% TiB 2 -SiC preform were inaccessible to the displacement of Al. The residual porosity of Al/TiB 2 -SiC composites was highly influenced by porous structure of TiB 2 -SiC preforms, including pore diameter, open porosity, close porosity and pore diameter. For 15% and 20% TiB 2 -SiC preforms, the unimodal pore volume distribution was most favorable for Al infiltration to get dense materials. Fully infiltrated composites resulted in low residual porosity. Nevertheless, Al/TiB 2 -SiC composites presented a significant increase in porosity with further increasing TiB 2 contents. It could be concluded that, compared with porosity of preforms, bimodal PSD of 30% TiB 2 -SiC preform which had small-size pores among TiB 2 -TiB 2 particles interactions was the main reason that increased the permeation resistance during infiltration which was undesirable for the densification of composites [43].
20% Al/TiB 2 -SiC composite reached a maximum density of 3.06 g/cm 3 with only a slight improvement compared with 15% Al/TiB 2 -SiC composite (3.05 g/cm 3 ). The full Al infiltration resulted in a high density of 15% and 20% Al/TiB 2 -SiC composites. The reduction of density was consistent with the increase of porosity with further increase in TiB 2 content. The high porosity of 30% Al/TiB 2 -SiC composites resulted in decreasing density of 2.8 g/cm 3 . Porosity was the main reason that determined the density of 25% and 30% Al/TiB 2 -SiC composites instead of the three phase contents. Figure 6(a) presented SEM images of 25% Al/TiB 2 -SiC composite on polished surface. Micrograph mainly displayed three different-contrast phases in Al/TiB 2 -SiC composite. The bright-gray finer TiB 2 particles whose size was around 2 µm or less were obviously on the polished surface with a homogeneous distribution. The fine-size in-situ formed TiB 2 and consequent homogeneous structure of TiB 2 -SiC porous ceramic had direct influence on the structure of Al/TiB 2 -SiC composites. Pores in the interconnected TiB 2 -SiC porous preforms were filled with Al. However, some unfiled pores were still observed on the surfaces.
EDS spot analysis using a big spot size was marked in Figure 6(a). EDS pattern corresponding to scanning plot in Figure 6(b) to get the element contents of all Al/TiB 2 -SiC composites. Volume fractions of Al, TiB 2 and SiC were obtained based on measurements of the elemental contents of Al, Ti and Si. EDS analysis results of the phase content were normalized with respect to the porosity to minimize the limitation [44] in Figure 6(c). Measured value of volume fraction of insitu formed TiB 2 is always a little higher than the theoretical value. The SiC content decreased correspondingly. 20% Al/TiB 2 -SiC had the highest Al content, then with the increase of TiB 2 content, the Al content decreased. High porosity and pore size increased the Al volume fractions in composites.
High-magnification micrograph (Figure 7(a)) and EDS line scan analyses (Figure 7(b)) were employed to identify different-contrast regions. The blue, red and green color EDS line profiles were corresponding to Ti, Al and Si element rich regions. The blue line marked the peak in the Ti richest region which corresponded to the bright-gray TiB 2 particles. The   The hardness of Al/TiB 2 -SiC composites possessed comprehensive influence which was mainly attributed to the phase contents, different ceramic grain hardness and pores distribution. Sintered pure TiB 2 had a higher theoretical hardness value of ~32 GPa compared with sintered pure SiC (~26 GPa) [45]. The largest grain sizes of sintered SiC and the least volume of TiB 2 particles in the composites were the reason for the low hardness of 15% Al/TiB 2 -SiC composite. With only a slight difference in porosity, 20% Al/TiB 2 -SiC composite reached the higher hardness, mainly due to the increasing TiB 2 particles which possessed a high hardness value. But with further increase in TiB 2 content, comparatively decrease in hardness was observed. The residual pores [46] in 25% and 30% Al/TiB 2 -SiC composites composite were the main reason for the reduced hardness value. This was verified by Paneto et al. [47] that the most important factor which determined the hardness value was the porosity. Figure 8(b) presented a representative Vickers hardness indentation micrograph on the polished surface of 20% Al/TiB 2 -SiC composite. Compared with the typical brittle fracture crack with one crack protruding from each corner of the indent [48], a special discrete micro-crack path showed along the diagonals of the indent. The multiple micro-cracks distribution around the hardness indentation periphery implied that ceramic ligaments in small regions easily deformed, but easily restricted by the boundaries and metal phase. Moreover, no crack propagation at four diagonals indicated that the interpenetrating structure of Al/TiB 2 -SiC composites effectively stopped the crack propagation by the interlocked boundary of the ceramic and metal phases [49].
The indentation feature with multiple cracks along the diagonals which effectively consumed energy was correspondingly associated with enhanced fracture toughness. Pan et al. [50] also verified the toughness enhancement of (TiB 2 +SiC)/Ti 3 SiC 2 composites which presented similar indentation morphology and the . The indentation impression morphology showed typical isotropic interpenetrating structure characteristics with micro-crack easily initiated in ceramic but hard to propagate continuously through the co-continues phases distribution. Asl et al. [49] also observed the interpenetrating structure effect on the crack propagation along hardness indentation with the ZrB 2 -SiC-C f composites. Figure 9 showed the flexural strength and fracture toughness of Al/TiB 2 -SiC composites with different TiB 2 contents. Both of them firstly increased, then decreased with increasing TiB 2 content. 20% Al/TiB 2 -SiC composite reached the optimum flexural strength of 399.4 MPa due to the relatively low porosity and full infiltration of Al. Meanwhile, compared with 15% Al/TiB 2 -SiC composite the increasing TiB 2 content was the reason for the increasing strength of 20% Al/TiB 2 -SiC composite. However, flexural strength values of 25% and 30% Al/TiB 2 -SiC composites continually decreased with increasing TiB 2 contents. The increasing residual pores were considered as the major influencing factor that  The existence of the bimodal pore size distribution and abundant small-size pores impeded the Al infiltration and full densification of 30% Al/TiB 2 -SiC composite [51]. Thus, the highest residual pores resulted in the lowest flexural strength of 30% Al/TiB 2 -SiC composite although 30% TiB 2 -SiC preform showed the highest strength. On the other hand, 25% Al/TiB 2 -SiC composite obtained the optimum fracture toughness value of 7.12 MPa ffi ffi ffi ffi m p . The improvement of the fracture toughness of 25% Al/TiB 2 -SiC composite was mainly attributed to the full infiltration of Al, increasing TiB 2 particles and the decrease of ceramic grain size. In addition, the increasing grain boundary free energy caused by grain refinement of ceramic particles could dissipate more energy by inducing more intergranular cracks, which could be the reason that the fracture toughness value of 25% Al/TiB 2 -SiC composite was a little higher than that of 20% Al/TiB 2 -SiC composite [52].  To further identify the composition and distribution of ceramic and metal phases on cross-sectional views, EDS mapping was applied on the fracture surfaces of 20% Al/TiB 2 -SiC composite as shown in Figure 10. The distribution regions of Ti, Si and Al elements were apparently visualized and applied to stand for where TiB 2 , SiC and metal aluminum existed in the Al/TiB 2 -SiC composites. The results of EDS mapping were consistent with line scanning analyses and clearly revealed topologically co-continuous phase distribution. Elemental distributions demonstrated that the red regions represented the ductile aluminum ligaments, the green color area showed the SiC distribution, and discrete light blue dots were TiB 2 particles. Accordingly, fracture surface was composed of three kinds of surfaces: SiC transgranular cleavage and TiB 2 intergranular fracture occurred in a brittle manner in advance, and Al tear-ridges occurred in a ductile manner. SiC was the main phase which possessed the most volume fraction with smooth surfaces on the fracture surface of 20% Al/TiB 2 -SiC composite. Fine-size TiB 2 particles uniformly distributed. The TiB 2 -SiC ceramic matrix was highly susceptible to crack propagation. It was obviously presented that Al located around the ceramic segments connected tightly without observable pores or gaps. Figure 11 revealed comparison of different Al/TiB 2 -SiC composite fractographic at different magnifications to investigate the fracture characteristics.
Smooth and flat cleavage surfaces were observed on the fractural microstructures of 15% Al/TiB 2 -SiC composite as shown in Figures 11(a, b). This fracture feature suggested lower fracture toughness. The in-situ formed TiB 2 presented fairly uniform distributions in 15% and 20% Al/TiB 2 -SiC composites. Additionally, it was worth noting that hemispheric holes caused by pull-out of TiB 2 particles were left on the fracture surfaces as shown in Figures 11(d, h). As typical intergranular fracture feature, pull-out of TiB 2 particles indicated a relatively low interfacial strength between TiB 2 and SiC phases. The pull-outs of fine-size TiB 2 significantly contribute to the enhancement of the Al/TiB 2 -SiC composites strength and toughness [53].
After the failure of ceramics, Al was pulled up into raised ridges [54]. As Al stretched plastically to failure, numerous fine-size tear ridges were left which were observed across the whole fractured surfaces near the interface of ceramic ligaments as shown in Figures 11(c) and (d). It was worth noting that the Al was not deboned from the ceramic phase even after severe plastic deformation. Moreover, there were no dimples originated in aluminum phase [55]. This phenomenon revealed that the crack not initiated from Al during the fracture process. Additionally, severe plastic deformation of metal had been considered to account for a major proportion of the energy dissipation in cleavage crack propagationwhich verified the toughening function of Al.
There were no evident residual pores on the fractural surface of 15% and 20% Al/TiB 2 -SiC composites which indicated full infiltration of molten aluminum alloy in porous preforms. The dense interpenetrating structure was expected to improve the strength of composites. With increasing TiB 2 content, due to the inhibition of SiC grain growth [56], the flat cleaver fractured surfaces area decreased. The transgranular fracture was more gradually mixed with increasing intergranular fracture mode. As a consequence, corresponding fractural surface of 25% and 30% Al/TiB 2 -SiC composites exhibited rugged surface as shown in Figures 11(e) and (g).The number of residual pores increased remarkably of 30% Al/TiB 2 -SiC composites which were clearly identified from high-magnification micrograph in Figure 11(h).
A tortuous crack path and crack tip shielding phenomena of secondary cracks closed to the main crack were depicted in Figure 12 to investigate the fundamental toughening mechanisms of interpenetrating composite. Figure 12(a) presented the main crack and the region with micro-cracks nearby. For the high-magnification of the crack in Figure 12(b), multiple cracks propagated through SiC grains, detoured at TiB 2 particles, and the crack tip generally stopped by aluminum which were all repeatedly observed. Crack deflected along TiB 2 particles was observed behind the crack tip. Crack branching was also clearly visualized when the crack front encountered the isolated TiB 2 particles.
The observed toughening mechanisms in the form of crack deflection, crack bridging and crack branching forced the cracks to propagate in a nonplanar fashion which increased the crack propagation path. Those basic fracture mechanisms were mostly related to the occurrence of TiB 2 particles instead of big-size SiC grains or ceramic phase boundaries. The in-situ formed finer TiB 2 particles and increasing TiB 2 contents were beneficial for the increasing number and reduced distance of toughening events which consequently consumed the additional fracture energy and greatly increased the toughness.
Uncracked-ligament bridging of ductile Al effectively provided enhanced resistance to crack propagation in ceramic ligaments resulting in a major improvement of toughness. Continuous ductile Al network restricted the short crack propagation everywhere and stabilized the catastrophic failure of brittle ceramic skeleton. As a consequence, long crack was hard to continuously form.
The presence of large amount of in-situ synthesized TiB 2 particles was beneficial for the increase in the number of crack deflection and branching events which consequently improved the fracture toughness and strength of composites [48]. The continuous interactions of crack with TiB 2 , Al and phase boundaries were the typical characteristics of the isotropic interpenetrating structures. The number of micro-cracks as a result of the extended crack propagation subsequently increased and dissipated more energy resulting in a high fracture toughness [57].

Conclusions
The Al/TiB 2 -SiC interpenetrating phase composites were successfully prepared by pressure-infiltration process of Al into in-situ synthesized TiB 2 -SiC preform. The main conclusions of this work were summarized as follows.
(2) XRD results showed that TiB 2 -SiC preforms were in-situ synthesized using TiO 2 , B 4 C, C 12  for fracture toughness, respectively. The optimum properties were attributed to the high open porosity, uniform pores size distribution and large pore diameter in 20% TiB 2 -SiC preforms that were beneficial to Al infiltration. (4) Characteristics of fractured micrographs showed a mix mode of trans/intergranular fracture in ceramic phases and ductile tearing fracture in Al. Toughness improvement of Al/TiB 2 -SiC composites was mainly determined by the fully infiltrated ductile aluminum. And the presence of the multiple phase interfaces as a result of interpenetrating structure also increased the toughness by resisting the crack propagation. In particular, in-situ TiB 2 particles could synergistically increase the fracture toughness based on crack branching, bridging and deflection.