Sustainable mechanical properties evaluation for graphene reinforced Epoxy/Kevlar fiber using MD simulations

Abstract Uniform filler dispersion and fillers, such as nanomaterials, with distinct but superior qualities compared to the typical matrix component can be used to create high performance composites. The current study used molecular dynamics simulations to investigate the effect of graphene reinforcement on the mechanical properties of Kevlar/Diglycidyl Ether of Bisphenol-A (DGEBA). Diethyl toluene diamine (DETDA) serves as the curing agent for DGEBA, and graphene is randomly reinforced at 1, 1.5, and 2 weight percent in the DGEBA/DETDA epoxy matrix. A layered (epoxy-Kevlar-epoxy, EKE) is constructed by maintaining Kevlar fibre in horizontal position in between the graphene-reinforced DGEBA/DETDA as illustrated in the figure. Energy minimization, geometry optimization, and dynamics are used to further stabilise the constructed structure. The method of constant strain is used to determine mechanical parameters. The MD simulation revealed that mechanical properties increased with increasing graphene content, with 21.42%, 36.47%, and 42.49% for 1, 1.5, and 2 weight percentages of graphene, respectively, when compared to pure EKE. The increasing trends in elastic moduli corroborate the experimental findings. The ultimate strength increases as graphene content increases.


Introduction
High performance composites can be produced by uniform filler dispersion and when the filler, i.e. nanomaterials, has different but superior properties to the standard matrix component.They are now useful in a variety of fields, including biomedical, sensing, energy conversion and storage, structural components with a high strength-to-weight ratio, and so on.Recent developments have also led to their use in gas barriers, food packaging, environmental protection, biomedical materials and making things less likely to catch fire [1][2].Nanocomposites are multiphase materials formed by combining a matrix and a nano-dimensional material.A nano-dimensional material could be carbon nanotube, graphene, nanoplatelet, nanofibers etc.The reinforcement of these materials significantly improves the mechanical properties as well as the electrical and thermal conductivities of the base composite [3].Over the last few decades, much research has been conducted on polymer nanocomposites, with graphene, carbon nanotubes (CNTs), molybdenum disulphide, and tungsten disulphide used as reinforcements to fabricate mechanically strong polymeric nanocomposites.Since the discovery of carbon nanotubes [4][5][6], a significant amount of study has been carried out with the majority of the work finished in the previous two decades.CNTs benefit from a variety of mechanical properties, including high stiffness and tensile strength, as well as the ability to withstand large deformations without fracture.Researchers discovered single-walled carbon nanotubes (SWCNTs) with diameters ranging from 1 nm to 2 nm and some of the highest values of Young's modulus, around 1 TPa [7][8].This can be accounted to their plastic [9], and their fracture behavior under tensile loading [10].They are also well-organized and have a high aspect ratio.Its tensile strength is nearly 150 GPa because it can withstand up to 15% tensile strain before fracture.This is possible because carbon nanotubes can release high stresses through a process known as elastic buckling [11].CNTs have a thermal conductivity of 1800-6000 W (m-K) at room temperature, demonstrating their significance in thermal properties as measured by experimental measurements and theoretical calculations [12][13].Because improving mechanical properties is of particular interest in this paper, observations of CNTs imparting their appealing mechanical properties to brittle materials have been made.As a result, it is a promising filler for polymer nanocomposites.Moreover, numerous industries, including as strain sensing [14], supercapacitors [15], EMI shielding, aerospace applications [16], and high-tech sporting goods [17], have benefited from the use of CNT-Polymer nanocomposites.
Polymers and resins were also thought to be blended with CNTs in order to impart their qualities into the matrix for load bearing purposes [18].The addition of roughly 1 weight percent (wt.%) of multi-walled carbon nanotubes (MWCNTs) to epoxy resin, for instance, boosted its stiffness and fracture toughness by 6% and 23%, respectively [19][20].Haggenmueller et al. [21] used a combination of solvent casting and melt mixing to scatter SWNT materials in PMMA.The process also included spinning the composite fibres with a melt spinning technique.The elastic modulus and yield strength of the composite were measured, and the results showed that the properties improved significantly as the percentage loading was increased.A SWCNTs-isotactic polypropylene (iPP) composite was made by Manchado et al. [22] using shear mixing.The findings showed that the Young's modulus increases in parallel with the SWNT loading in the polymer matrix.The outcomes also demonstrated that the IPP's tensile modulus improved by 40%, from 0.85 GPa to 1.19 GPa, with a nanomaterial content of 0.75% by weight in the composite.Cadek et al. [23] performed tensile tests on composite films made of polyvinyl alcohol (PVA) and six different types of carbon nanotubes at various nanotube loading levels.The tests revealed that the Young's modulus increased by a factor of two in all cases.Blake et al. [24] discovered significant improvements in Young's modulus, strength, and toughness for PVC-based composites reinforced with chlorinated polypropylene grafted carbon nanotubes.Wu and Xu [25] performed MD simulations using Dreiding2.21and advanced compass force-field on DGEBA/DETDA.The authors have achieved conversions up to 93.7%.Significant improvement was observed on the elastic modulus with degree of conversion.The nano-indentation hardness of the composite above the isolated polymer was increased by 271%, according to research by Gupta et al. [26] on composites comprised of a PU polymer matrix and MWCNT fillers.Additionally, the authors found that a composite loaded with 10 weight percent MWCNT outperformed neat polymer composite in terms of elastic modulus by 290%.Navneeth et al. [27] conducted a number of tests on nanocomposites, including epoxy and polyester nanocomposites with and without CNT reinforcement.Tensile, flexural, shear, and impact tests were performed.In all of the tests, the nanocomposites outperformed the polymers alone.When compared to the Polyester nanocomposites, the Epoxy nanocomposite produced better results.Patel et al. [28] studied 0.1 wt.% Poly(methyl methacrylate) (PMMA)/CNT nanocomposites injection moulded from micro compounders with a co-rotating twin screw extruder.Significant improvement was observed in tensile, fracture, and compressive strength of the reinforced polymer over the pure polymer.Dikshit et al. [29] developed an epoxy, DGEBA, as a matrix that was hardened with DETDA and reinforced with CNT.MD simulations were used to predict the mechanical properties, which were then compared to the properties of epoxy without reinforcement.The study found that the Young's modulus improved from 2.429 GPa for the non-reinforced epoxy to 13.27 GPa for the reinforced epoxy (DGEBA-DETDA) nanocomposite.Furthermore, as the stain amplitude increased, the Young's modulus of both models decreased.
Aromatic polyamides are referred to as 'aramid fibres' (Afs).These synthetic fibres have a high level of heat resistance, making them a good and trustworthy choice for aerospace and defence technology.These are also utilised for ballistic purposes in the present-day technological period, which ultimately results in rated body armour fabric.Afs have low electrical conductivity and behave as insulators.Due to its chemically inert surface, it has the significant drawback of poor adhesion.The surface adhesion is being improved by researchers employing a variety of techniques, such as chemical activation [30].Additionally, several studies demonstrate that aramid fibres can be strengthened with nanomaterials like CNTs to increase their electrical conductivity [31].Kevlar is a synthetic fibre that is both heat-resistant and exceptionally strong.It is a type of para-aramid that is also known by the chemical name PPTA.In the beginning, it was utilised in the tyre industry as a substitute for steel.Although it is possible to employ this as a matrix in composites, very little research has been done on the subject.In order to make hybrid composites, it is combined with other matrix materials and utilised as a co-matrix.When it is spun, it possesses a tensile strength of 3.62 GPa and a relative density of 1.44 g/cm 3 [32].It finds use in a variety of industries, including the ballistics fabrics [33], the automotive industry, and the acoustic industry.Kesiya et al. [34] found that the tensile strength of an EPDM/Kevlar fibre hybrid that was reinforced with nano-silica as a filler had approximately a 109% surplus over its original value.Abdel-Mourad et al. [35] conducted research on the resistance to damage of a number of different nano-fillers when combined with Kevlar KM2 plus/epoxy nanocomposite.The laminated Kevlar/epoxy composite with 0.5 wt.% of MWCNT had the best results when it came to the material's resistance to damage.Taraghi et al. [36] had reported that the elastic and bending modulus of woven Kevlar/epoxy can be improved by 20% and 40%, respectively, by adding a small amount of MWCNT (less than 1%).The impact strength increased by 45%.The authors have further revealed that the greatest improvements were noticed for a MWCNT concentration of 0.5%.Alsaadi et al. [37] found that the mechanical properties, such as tensile strength, flexural strength, flexural modulus, and toughness, all increased by 6.1%, 31.1%,8.7%, and 11.8%, respectively, when 0.25 wt.% of graphene nanoplatelets were reinforced in Kevlar epoxy nanocomposite.Sharma et al. [38] reported a 56% increase in elastic modulus at 0.3 Wt.% MWCNT reinforced Kevlar-epoxy nanocomposite.The increased elastic modulus was attributed to improved interfacial properties between the Kevlar fibre and the epoxy matrix.Madarvoni et al. [39][40] conducted DMA analysis on carbon, Kevlar, and hybrid fabrics reinforced with graphene and hexagonal boron nitride and discovered that mechanical properties such as storage modulus and loss modulus increased by 49% and 38%, respectively.Shiju et al. [41] investigated the thermal mechanical properties of a Kevlar-Nomex copolymer using graphene oxide platelets.According to the authors, there was a greater shift in glass transition temperature and improved interfacial interaction between the matrix chain and the reinforcement.
According to the existing literature, the experimental investigation reveals that various nanostructures such as graphene (Gr), hexagonal boron nitride nanosheets (h-BNNS), and carbon nanotubes (CNTs) may improve the mechanical and thermal properties of Kevlar fiber-epoxy nanocomposites.The experimental investigations have not revealed the failure mechanisms of these nanocomposites.The failure of EKE can be studied at the atomic level.Furthermore, the experimental procedures are very expensive in terms of setting the process parameters.There is very little research based on MD simulations to study the mechanical properties of EKE nanocomposites.In the present research, the authors have made an effort to use MD simulations to build a single layer EKE nanocomposite.The layers produced resemble the experimental technique known as the hand layup process.Gr was previously reinforced in the DGEBA/DETDA matrix at weight percentages of 1, 1.5, and 2, and the layer was created in the Material Studio environment.The prepared layer was further processed to obtain the mechanical properties.This study is the first of its kind which may provide a complete explanation of the failure mechanism of Gr reinforced DGEBA/DETDA-Kevlar fiber, taking into account the interaction between DGEBA/ DETDA and Kevlar fibre.The manuscript is organised as follows: Specific introduction and literature are presented in section 1; atomistic modelling of DGEBA, DETDA, Gr, and Kevlar fibre and methodology are presented in section 2; construction of DGEBA/ DETDA-Kevlar-DGEBA/DETDA layer at different Gr content is presented in section 3; simulation results and discussion are presented in section 4; and conclusions are presented in section 5.

Modelling and methodology
In the present research, MD simulation has been performed to study the mechanical properties of Gr and h-BNNS reinforced Kevlar-epoxy nanocomposite.The atomistic models have been created using the Material Studio software and further simulations were done using Large-scale Atomic/Molecular Massively Parallel Simulator (LAMMPS).MD is a computer simulation method which is used to analyze the physical movements or motions of atoms and molecules.The analysis is simulated by allowing the atom and molecules to interact with each other for a fixed amount of time.This is followed by solving Newton's equations of motions to determine the trajectories of atoms and molecules.It employs the usage of interatomic potentials or force fields to calculate the forces or potential energy between interacting particles.
Diglycidyl Ether of Bisphenol-A (DGEBA) has been selected epoxy for the reinforcement purpose.DGEBA is a thermosetting polymer which is extensively used in aerospace and electronics industries for adhesives, composites, coatings etc.It has excellent cross-linking properties and an irreversible network structure that forms polymer chains when chemically reacting with hardeners such as amines and anhydrides.The resultant compound exhibits exceptional thermomechanical and structural properties.The properties of the final compound closely depend on the cross-linking and network structure [42].In pure form, DGEBA is a weak material, and its rigidity may be increased by curing with a suitable hardener considering the cross linking properties.In the present research, Diethyl toluene diamine (DETDA) is selected as the hardener due to its superior properties over other hardeners.In the MD method, the curing of the DGEBA and DETDA may be achieved in two methods.In first method includes sketching of the individual molecule of DGEBA and DETDA and manually creating the crosslinked structure based on the possible degree of cross-linking.The created structure is further used for constructing a simulation volume called an amorphous cell with periodic boundary conditions with an initial density lower than the actual density and desired number of molecules.The constructed amorphous cell also defined as the representative composite and MD simulations such as energy minimization, geometry optimization, dynamics, etc. run for stabilizing the model and further used for predicting various mechanical, thermal, and physical properties [43].In the second method, creating a representative simulation volume with primary molecules of DGEBA and DETDA without any manual crosslinking and imposing various minimization and equilibrium runs to achieve a certain degree of cross-linking.The mechanical, thermal, and physical properties are predicted after running several MD simulations steps.
The second method is relatively cumbersome than the former method which is realistic and more accurate [44].However, the degree of cross-linking is influenced by several parameters such as cut-off distance, the ratio of hardener and epoxy, and reaction priorities.The first method is used in this study to obtain the simulation volume with chemically cross-linked DGEBA and DETDA.First, in a material studio environment, an atomistic model of DGEBA and DETDA was created.Three molecules of DETDA and seven molecules of DEBGA were used to create a rigid triangular model [45] as shown in Figure 1(a).Mechanical properties of the pure DGEBA/DETDA are very low [46][47] which can be enhanced by reinforcing with the nanomaterials such as Gr, CNT, and h-BNNS etc., which has superior mechanical properties.Graphene (Gr) has been demonstrated as one of the potential reinforcement materials for improving the mechanical properties of epoxy, which has an exceptionally high stiffness and strength The influence of Gr reinforcement in DGEBA/DETDA matrix is well established in the previous literature [47][48][49]57,58].Thus, based on previous literature, in the present research, DGEBA/ DETDA is randomly reinforced with 1%, 1.5%, and 2% Gr. Figure 1(b) depicts the atomistic model of Gr.The amorphous cell module is used to reinforce the DGEBA/DETDA at a lower density than the actual density.The created model is the representative composite, which is then simulated using energy minimization, geometry optimization, and dynamics.At room temperature, the dynamics are run using a normal temperature pressure (NPT) ensemble.The total simulation time was 10 Pico seconds (ps), with a time step of 0.1 femto seconds (fs) and a total of 100,000 steps.
An atomistic representation of the Kevlar molecule with a chain length of five was constructed within the environment of Material Studio.A representation of an atomistic model containing a repetition unit, head, and tail atoms may be seen in Figure 2.
The created Kevlar homopolymer is put into the simulation cell with a loading size of 10 polymers and simulated further to achieve an experimental density equivalent to that of the real Kevlar polymer.The simulated density is found to be 1.33 g/cm3, which is very close to the experimental density of 1.44 g/cm 3 [39] shown in Figure 3.

Modelling of epoxy-Kevlar layered composite
To obtain the coating of Gr reinforced DGEBA/DETDA on the Kevlar fibre, a layer was formed with the Kevlar fibre sandwiched between the Gr reinforced DGEBA/DETDA.The layers are referred to as EKE0, EKE1, EKE1.5, and EKE2 based on the wt.% of Gr, where EKE represents epoxy-Kevlar-epoxy and the numeric value represents the wt.% of Gr in epoxy.Energy minimization, geometry optimization, and dynamics are used to stabilise the developed model using the COMPASS II forcefield [52][53].From the previous literature [24,41,[47][48][49][54][55][56] it has found that COMPASS II is the most suitable  forcefield for polymers which has given satisfactory results for variety of polymers.Moreover, COMPASS II contains a 22 classes of polymers which includes 144 homopolymers and 297 copolymers.
The dynamic simulatuion was conducted using NPT ensemble at room temperature (300 K).The control parameters setting for dynamics run are shown in Table 1.Number of atoms at different reinforcement of Gr, final density, initial and final cell parameters are dipicted in Table 2.The geometric structures of EKE1, EKE1.5, and EKE2 before and after the equibilaration are shown in Figure 4(a-f).For all the structures, the convergence analysis has been done in geometric optimization steps.The structures converged at 4000 of the optimization steps.From Figure 4 it can be seen that there is small change in the Kevar layer after dynamics simulation which may be due to the application of compressive force.The dynamics simulation results for EKE1, EKE1.5, and EKE2 are shown in Figure 5(a,b).It can be seen that the developed molecular model becomes stable with simulation time.It has been found that the energies of the developed model initially fluctuate with simulation time and become stable as the simulation progresses, as shown in Figure 5(a) for all the three structures EKE1, EKE1.5, and EKE2.The lower the energy, the higher the stability of the model.The kinetic energy of the model is very low, which shows the stability of the model.The non-bond energy was found to be almost constant throughout the simulation, which supports the claim.Since the simulation was performed     at room temperature, the final temperature of the model should have been 300 K.A large fluctuation in the model temperature was observed with the initial simulation, resulting in further energy loss.However, the model stabilised near room temperature, as shown in Figure 5(b).The four models EKE0, EKE1, EKE1.5, and EKE2 have final simulated densities of 1.27, 1.29, 1.33, and 1.26 g/cm 3 , respectively, which is very close to the experimental density of 1.44 g/cm 3 of pure Kevlar.

Results and discussion
To predict the mechanical properties using the MD simulations three methods viz.constant strain minimization, constant stress, and fluctuation methods are widely used.In the present research constant strain minimization method has been employed with six strain patterns.Some assumptions in this method include the fact that deformation of fixed bond length and angle, as well as configurational entropy, have a negligible impact on mechanical properties such as elastic modulus [24,48].A small deformation of 0.003 strain amplitude within the elastic range has been applied on the stabilized structures EKE0, EKE1, EKE1.5, and EKE2.Beforehand, the simulated model was allowed for pre-minimization using the smart algorithm without change in geometric properties such as cell parameters.The pre-minimization was run to ensure the prediction of mechanical properties for the most stable model.The possible agglomeration has been studied using the radial distribution function (RDF) which describes how the atoms are radially packed around each other in the system [50].The RDF study for the Gr reinforced DGEBA/ DETDA for 1.5 wt.% of Gr is shown in Figure 6.From Figure 6 it can be seen that there are three major peaks under 1.5 Å.The two major peaks are at very close distance 1.09 Å and 1.11 Å which reveals that the initial interaction is at the short range.No long-range bond formation occurred which shows that there is no agglomeration occurred and dispersion was adequate.Similar results were obtained for the 1% and 2% of Gr.
The stress-strain relationship in MD simulations for linear elastic materials is governed by Hook's law, which can be expressed in second order as: σ i and ε j represent the six-dimensional stress and strain vectors and C ij is a 6 × 6 matrix.The energy method was used to calculate the stiffness matrix which is given by [47]: For the isotropic materials, stress-strain behavior is represented by the Lame coefficients (λ, µ) as: λ, µ may be calculated from C ij as: Other important mechanical properties such as elastic modulus (E), shear modulus (G), bulk modulus (K), and Poisson's ratio (ν) may be derived from the Lame coefficients (λ, µ) as follows: The Lame coefficients (λ, µ) are identified from the stiffness matrix obtained by the MD simulation at a very small strain amplitude (0.003) using the constant strain method.The identified values are then used to calculate the various average mechanical properties using Equation (5).The simulated average elastic modulus of EKE0 was found to be 48.12GPa, which is higher than the experimental value (39.31GPa) as reported in [40].The simulated elastic modulus of 44.85 GPa was discovered by [40] using the mean-field homogenization method (Digimat software), which is quite similar to the outcome (48.12 GPa) of the current study.The experimental values of average elastic modulus depend on various parameters such as processing of epoxy and Kevlar, experimental setup, number of layers, etc., which may introduce defects in the experimental sample.In the present research, simulations have been carried out on a single layer (i.e. one crystal of EKE), which is defect free, thus resulting in a higher average elastic modulus than the experimental value.However, the average elastic modulus is smaller than the pure Kevlar.The experimental elastic modulus of pure Kevlar is 200 GPa [49] and MD simulation revealed 325 GPa for single layer crystal in the loading direction [50].The reduction in the elastic modulus may be due to the lower value of average elastic modulus of DGEBA/ DETDA (2.71 GPa [51, 59,60]).However, MD simulations reveals that there is significant enhancement in the average elastic modulus when Gr is added in the of EKE model.At 1%, 1.5%, and 2% of Gr reinforcement, the elastic modulus was found to be 58.43GPa, 65.67 GPa and 68.57GPa respectively.The increase in the elastic modulus is attributed to the increased interface properties and stress transfer from DGEBA/DETDA to the Kevlar fiber due to the increasing Gr content in the DGEBA/DETDA matrix.However, the triangular structure of DGEBA/DETDA provides more rigidity to the matrix, and the effective mechanical property of Gr is transferred to the DGEBA/DETDA matrix, which ultimately improves the elastic property of KEK and enables the matrix material to withstand loads, dispersion pressure, and external forces.Gr, on the other hand, may not interact with aliphatic polymer chains due to its nature.The carbon atoms in Gr are connected to one another by three sigma bonds, but the pi electrons, which are present above and below the sheets, are quite mobile.Figure 7 represents the comparison of elastic modulus of EKE0, EKE1, EKE1.5 and EKE2.The rate of increase in elastic modulus at 1 and 1.5% of Gr is more compared to the 2% Gr.This may be due to the short-range agglomeration of Gr at higher percentage.The agglomeration weakens the Kevlar-DGEBA/ DETDA interface and also cause for stress concentration.Moreover, the percentage change in elastic modulus is found to be 21.42%,36.47% and 42.49 for EKE1, EKE1.5 and EKE2 respectively compared to EKE0.The Poisson's ratio for all the EKE models was found to be in the range of 0.32 to 0.39.
The stress-strain pattern for Gr reinforced EKE nanocomposite is found to be linear as evident from Figure 8.As evident from Figure 8, the tensile strength of the EKE0 is 499.53GPa which increases with the addition of Gr.The maximum stress at break point of EKE 1, EKE1.5 and EKE2 are 958.65 GPA, 1291.89GPA, and 1765.75GPa respectively.The profile of stress-strain curve indicates that the nanocomposite has brittle nature.From Figure 8, it is also evident that the brittleness increases with the increasing content of Gr.In all the cases, as the Gr content increased, the strain rate fell.A similar observation was present in [40].In typical composites, interphase is primarily thought to contribute to the effect of load transfer.From the MD simulation, it is found that the stress carrying capacity increases with the Gr reinforcement which is attributed to superior interface properties of Gr reinforced DGEBA/DETDA and Kevlar fiber.Unlike to experimental results [36], the strength of the Gr reinforced EKE nanocomposite increases with Gr content which reveals that the addition of Gr enhances the interfacial as well as intermolecular properties and, thus, increase in the load carrying capacity.The ultimate strength of the Gr reinforced EKE is depicted in Figure 9 which also increases with the Gr content in EKE nanocomposite.However, the maximum strain amplitude for the ultimate strength decreases with an increase in the Gr content.EKE0 fails at strain amplitude of 0.012 while EKE1 and EKE1.5 fail at 0.01 strain amplitude respectively and EKE2 at 0.009 strain amplitude.

Conclusions
In the present research, DGEBA/DETDA was reinforced with Gr at three wight percent viz.1%, 1.5% and 2% in order to study the effect on the elastic modulus of layered  DGEBA/DETDA-Kevlar using the MD simulations.A layer of Gr reinforced DGEBA/ DETDA was applied on both sides of the Kevlar fiber and elastic modulus was predicted using the constant strain method using MD simulations.The following conclusions can be drawn from the present research: 1.The elastic modulus of the EKE increases with the increasing Gr content in DGEBA/DETDA.The percentage change in elastic modulus is found to be 21.42%,36.47% and 42.49 for EKE1, EKE1.5 and EKE2 respectively compared to EKE0. 2. The rate of increase in elastic modulus is more with 1% of Gr when compared to 1.5% and 2% of Gr amounting 21.42%, 12.39% and 4.41% respectively.3. The brittleness of the EKE increases with increasing Gr content and the maximum strain amplitude found to be 0.012 for EKE, 0.01 EKE1 and EKE1.5 while EKE2 fails at 0.009 strain amplitude.4. The MD simulation revealed that the ultimate compressive strength increases with increasing Gr content.
The current study used industrial recommendations to cross-link DGEBA and DETDA.Future research could investigate the effect of DGEBA/DETDA crosslinking and the reinforcement mechanism of Gr in the epoxy matrix on the elastic modulus of EKE.The predicted elastic moduli in this study are based on a single layer of EKE.The MD simulation can be run by stacking multiple layers.However, increasing the number of layers results in a greater number of atoms, which may necessitate more computational time.

Figure 7 .
Figure 7. Elastic modulus of EKE at various percentage of Gr.

C
Labesh Kumar is Assistant Professor in the Department of Mechanical Engineering, Institute of Aeronautical Engineering, Hyderabad, India.His core research expertise's are in the domain of Production Technology, Joining Process, Automation Quality Control, Advance Manufacturing, Industrial Management, Technology Management, Supply Chain etc.He has rich experience of 11 year in teaching and research.He has published many indexed papers in well reputed journals.Pankaj Sonia is Assistant Professor in the Department of Mechanical Engineering, GLA University Mathura, India.His core research expertise's are in the domain of Materials processing, composite development and synthesis, microstructural characterization and joining of materials.He has rich experience of 12 year in teaching and research.He has published many indexed papers and chapters in well reputed journals and books.Vimal Kumar Pathak received his Ph.D. degree in Mechanical Engineering (design) from MNIT Jaipur.He received his M. Tech degree from ISM Dhanbad, India.Currently, he is working as an Assistant Professor in the Department of Mechanical Engineering at Manipal University Jaipur, Jaipur, Rajasthan.His research interest includes optimization, soft computing, composites, metrology etc.He has published more than 70 articles in international Conferences and reputed Journals.Kuldeep K Saxena Prof. (Dr.) has done his B.Tech, in Mechanical Engineering and M.Tech in Material Science and Engineering from MNNIT Allahabad.He has completed his doctoral degree from IIT Roorkee.He has 13+ years of experience in academics, research and industry.Prof. Saxena holds expertise in hot deformation behaviour of materials, microstructural characterization of materials, and micro manufacturing.He has served as Senior Research Fellow (SRF) for 2 years and 8 months on a project sponsored by Board of Research in Nuclear Sciences (BRNS), a research unit of Bhabha Atomic Research Centre, Trombay, Mumbai.Dr. Saxena is an author of many book chapters published by reputed publishers such as Elsevier and many more.He has authored 292+ research papers which are published in reputed international journals indexed by SCI/ Scopus.He has organised many International Conferences in India and Abroad.He is currently working as Professor and Head, Department of Research Impact and Outcome (LFTS) in the Division of Research and Development, Lovely Professional University, Phagwara, India.He is an active member of The Indian Institute of Metals (IIM) and Secretary of The Indian Institute of Metals Mathura Chapter.He is also a guest editor in many reputed journals such as Journal of Process Mechanical Engineering (SAGE, SCI, IF 1.8), Indian Journal of Engineering and Materials Science (CSIR, SCI, IF 0.8), International Journal of Interactive Design and Manufacturing (Springer, Scopus & ESCI), Materials today Proceedings at Elsevier platform and many more.Sana Sulaiman Hamid is from Iraq, She is 29 years old, She has received his PhD.from Turkey, and a Master degree from Iraq, Baghdad.She has many research papers on the subject of data aggre-gation, wireless sensor, BEE, optimization technique, right now She is a Faculty on Al-Farahidi University, Communication Technical Engineering, Baghdad, Iraq.N. Ummal salmaan is Assistant Professor in the Department of Automotive Engineering, Aksum Institute of Technology, Axum, Ethiopia.His core research expertise's are in the domain of development of various types of composites and their synthesis, microstructural characterization, Materials processing and joining of materials.He has rich experience of 08 year in teaching and research.He has published many indexed papers and chapters in well reputed journals and books.

Table 1 .
control parameters employed for dynamics.

Table 2 .
Effect of dynamics run on intital and final structure of EKE.