Structure and properties of Sn-Cu lead-free solders in electronics packaging

ABSTRACT With the development of lead-free solders in electronic packaging, Sn-Cu lead-free solder has attracted wide attention due to its excellent comprehensive performance and low cost. In this article, we present recent developments in Sn-Cu lead-free solder alloys. From the microstructure and interfacial structure, the evolution law of the internal structure of solder alloy/solder joint was analysed, and the model and theory describing the formation/growth mechanism of interfacial IMC were introduced. In addition, the effects of alloying, particle strengthening and process methods on the properties of Sn-Cu lead-free solders, including wettability, melting and mechanical properties, were described. Finally, we outline the issues that need to be resolved in the future research.


Introduction
In the electronics industry, solder joints connect electronic components with the printed circuit boards [1]. Traditional Sn-Pb solder was widely used in the electronic packaging industry because of its performance advantages. However, with the increasing awareness of environmental protection, the toxicity of lead has attracted much attention. Japan, EU and other countries and regions have promulgated laws to gradually prohibit the use of lead in the electronic packaging [2][3][4][5][6][7]. These initiatives provide a good opportunity for the development of new lead-free solder. Hence Sn-base lead-free solders, including Sn-Ag [8], Sn-Bi [9], Sn-Cu [10], Sn-In [11], Sn-Sb [12] and Sn-Zn [13] have become the potential candidates for Sn-Pb solder replacement.
Compared with traditional Sn-Pb solder, Sn-Cu solders exhibit the higher melting point [14][15][16][17][18]. However, there is still potential for the further development of Sn-Cu solder alloys with higher properties.
The eutectic Sn-0.7Cu alloys have become the focus of research, since the eutectic alloys have the advantages of low melting point, narrow crystallization temperature range, good fluidity and low tendency of hot cracking and segregation. Among the new Pbfree alloy candidates, Sn-0.7Cu solders are inexpensive and exhibit promising characteristics [19]. As the practicability of Sn-Cu solder has been confirmed continuously, Sn-0.7Cu solder has been widely used in wave soldering process [20,21]. In order to research several properties of Sn-Cu solder alloys, a lot of researches have been done, including the structure/interface evolution, the wettability and mechanical properties, by means of alloying, particle strengthening and solidification rate control.
This article reviews the research progress of Sn-Cu solder alloys. The microstructure and interfacial evolution of solder alloy were summarized. The wettability, mechanical properties and melting properties of Sn-Cu lead-free solders were analysed. Combined with alloying and particle strengthening methods, the research results of modification of solders were discussed.

Microstructure
The research of microstructure is vital for evaluating lead-free solder since the microstructure of solder directly determines the properties of the solder and the solder joints. According to the phase diagram ( Figure 1 [22,23]), the stable intermetallic phases below 300°C are Cu 3 Sn and Cu 6 Sn 5 phases [24]. Sn-0.7Cu is near eutectic system and the main phases are β-Sn and Cu 6 Sn 5 at room temperature [25]. The eutectic reaction of L→β-Sn + η-Cu 6 Sn 5 exists in Sn-0.7Cu at 227°C. With the further cooling of the melt to 186°C, the transformation of the Cu 6 Sn 5 phase occurs from the hexagonal η-Cu 6 Sn 5 to a monoclinic polymorph η'-Cu 6 Sn 5 [26][27][28][29]. This solid phase transformation has a significant impact on solder joint reliability [23,30].
The effect of Cu content on the microstructure of Sn-xCu was investigated by Hung et al. [31]. It was found that the addition of Cu played a refining role on the β-Sn. Cu 6 Sn 5 increased with the increase of Cu content. For Sn-1.3Cu and Sn-1.7Cu samples, a large number of Cu 6 Sn 5 particles distribute evenly in the matrix and play a role of particle strengthening. However, with the increase of Cu content, the melting temperature of the solder alloy will increase significantly, which will directly affect the soldering temperature.
The remarkable effect of element doping on the equilibrium system of alloys, such as phase transformation and microstructural stability, has been widely confirmed [26,[32][33][34][35][36]. According to the solubility of alloying elements in Cu 6 Sn 5 , the doped elements can be divided into two categories: (i) Ni, Au, Sb, In, Co, Pt, Pd and Zn are easily dissolved in Cu 6 Sn 5 intermetallic compounds (IMCs); and (ii) elements (Bi, Ag, Fe, Al, P, rare-earth elements, Ti and S) have poor solubility in the Cu 6 Sn 5 intermetallic [37].
Al is often used in the study of lead-free solder because of its low density, good electroconductivity and thermal conductivity. It has been reported that the addition of Al in hypereutectic Sn-Cu solder alloys resulted in the remarkable refinement of primary Cu 6 Sn 5 grains since the introduction of δ-Cu 33 Al 17 or γ-Cu 9 A l4 with the significant undercooling structure before Cu 6 Sn 5 grain growth leads to the heterogeneous nucleation of Cu 6 Sn 5 [38]. Figure 2 depicts the microstructure of Sn-0.7Cu-xAl (x = 0~0.075) solder alloy [39]. The microstructures of Sn0.7Cu solder alloys are composed of β-Sn and Cu 6 Sn 5 /β-Sn eutectic composition, while the solidified Sn-0.7Cu-0.075Al alloy is composed of β-Sn, Cu 6 Sn 5 and δ-Al 2 Cu [40]. The Al addition makes the microstructures of the composite solder finer and the dispersion of Cu 6 Sn 5 IMC in the matrix of β-Sn as shown in Figure 2(c-f), which is caused by Al atoms dissolution into β-Sn and eutectic refinement. In addition, with the increase of Al concentration the volume fraction of eutectic phase increases and Cu atoms and Al atoms tend to segregate in a certain region. After the precipitation of Cu 6 Sn 5 IMC during solidification, Al 2 Cu phase was formed by the reaction of Cu 6 Sn 5 IMC and Al, which could inhibit the formation of Cu 6 Sn 5 phase.
The addition of appropriate amount of Ag to Sn-Cu solder alloy can promote the formation of network eutectic structure and heterogeneous nucleation reaction of β-Sn/Cu 6 Sn 5 and refine the grain size of β-Sn [41,42]. This change is mainly caused by the formation of Ag 3 Sn in the solder metal matrix. Figure 3 shows a typical scanning electron microscopy (SEM) micrograph of as-solidified Sn-0.7Cu solder alloy and the solidification structure containing Ag or In addition [43]. The average diameters of β-Sn grain and Cu 6 Sn 5 particles are 20-70 μm and 0.5-0.8 μm, respectively (as shown in Figure 3(a,d)). With Ag addition, a larger number and smaller size of IMC particles (Ag 3 Sn and Cu 6 Sn 5 ) are observed. In Sn-0.7Cu-2Ag solder, the number of Ag 3 Sn particles is more than that of Cu 6 Sn 5 particles due to the influence of interface energy [44]. Similarly, for Sn-0.7Cu-2In solder, γ-SnIn 4 IMC is found, which promoted the formation of eutectic regions on the surface of β-Sn matrix and inhibited the formation of large β-Sn dendrite cells. On the other hand, the addition of highly active In resulted in the formation of γ-SnIn 4 IMC, which reduced the activity of Sn, and ultimately inhibited the formation of Cu 6 Sn 5 IMC.
Zhu et al. [45] added micron-sized Zn particles to Sn-0.7Cu solder, and found that with the increase of Zn content, β-Sn refined continuously. This is because the addition of Zn increased the number of nucleation particles, resulting in the grain size of the primary crystal of β-Sn gradually reduced, inhibiting the growth of β-Sn phase. But when the content reached 0.2%, β-Sn phase tended to coarsen. The shear strength of solder was improved to a certain extent because the undercooling of solder was  restrained and the microstructure was refined, which strengthened the blocking effect of grain boundary on dislocation. The formation of Cu 5 Zn 8 particles caused by Zn addition trapped in the Cu 6 Sn 5 grain boundary and played a dispersion-strengthening role [46]. The author held that the addition of Zn should not be excessive. From the microstructure of Sn-0.7Cu-1.0Zn, the size of Cu 5 Zn 8 particles began to show coarsening. If further increase the Zn addition, the size of Cu 5 Zn 8 particles in the microstructure will be further increased, and the properties of the solder will deteriorate because Zn is easy to be oxidized.
As a metal element adjacent to the Cu element, Ni has the same atomic radius and similar structure and properties. Therefore, Ni is also used as the addition element in the modification of Sn-Cu alloy. In general, the Cu atom in the solder alloy can be replaced by nano-Ni particles, and a small amount of dispersed (Cu,Ni) 6 Sn 5 phase can be formed in the primary phase and network eutectic structure, which can refine the primary β-Sn phase. A cellular-type eutectic microstructure was observed in Sn-0.7Cu-0.05Ni solder casting [47]. With the increase of Ni content (0-0.1wt.%), the volume fraction of primary β-Sn decreased gradually so that the more eutectic structure was observed in the microstructure of Sn-0.7Cu-xNi solder [48]. In addition, a microstructural feature named 'coral zones' was observed in the Nicontaining alloys, which contain significantly smaller intermetallics. While the formation mechanism of the coral zones is not yet clear.
Ge et al. [49] found that Fe particles addition can effectively improve the microstructure of Sn-0.7Cu solder matrix. With the addition of 0.025% Fe particles, the Cu 6 Sn 5 grains inside the solder appear as needle in the β-Sn matrix. When the content of Fe particles reaches 0.05%, the shape of Cu 6 Sn 5 changed and distributed in the β-Sn matrix. With the further increase of Fe, the microstructure of the solder alloy has coarsened. This happened mostly because Fe easily reacts with Sn forming FeSn 2 phase, which changes the original microstructure balance of the solder. Tsao et al. [50] reported the effect of nano-TiO 2 particles addition on the microstructure of Sn-0.7Cu solder. Adding appropriate amount of TiO 2 particles can effectively refine the β-Sn matrix, inhibit the growth of Cu 6 Sn 5 grains and advance the fine Cu 6 Sn 5 grains dispersing in the β-Sn matrix. According to Table 1, with the increase of TiO 2 content, the average grains size of both Cu 6 Sn 5 and β-Sn decrease significantly. The decrease of average spacing of Cu 6 Sn 5 IMC means that the number of Cu 6 Sn 5 IMC increases. In addition, the eutectic area is increased by 125% (30 ± 7% of Sn0.7Cu solder vs. 68 ± 7% of Sn0.7Cu-1TiO 2 solder).
Rare earth (RE), and especially lanthanide elements are invaluable in the development of new leadfree solders, and have attracted attention of many researchers [51]. The effect of Ce and La on the microstructure and mechanical properties of Sn-0.7Cu alloy were researched [52]. When the addition of RE reaches 0.5%, β-Sn phase is refined obviously. The radial grain size is reduced from 30-50 μm to 5-10 μm, and the IMC Cu 6 Sn 5 is fine and uniformly distributed in the β-Sn matrix, as shown in Figure 4.
The effect of Pr on the microstructures of Sn-Cu-Ni solders was investigated [53]. Figure 5 shows the matrix β-Sn and IMC phases (Cu 6 Sn 5 , (Cu, Ni) 6 Sn 5 ) distributing between the β-Sn grain boundaries in microstructure of as cast alloy. The grain size of β-  Sn is refined and the structure of solder alloy exhibits more uniform. When Pr content is 0.05%, the alloy shows favourable properties, which may be due to the refining influence of rare earth elements on the solder matrix and the nucleation and growth of PrSn 3 IMC. Similar to Pr, the addition of Nd can effectively refine the matrix of Sn-Cu-(Ni) solder [54]. As Pr and Nd have the surface activity, they tend to aggregate at the frontier of solidification interface during the solidification process, which increases the composition of solder alloy supercooling, and some crystals appear cystiform growth instead of the original flat growth pattern, reducing the dendrite spacing and refining the matrix structure. Rare earth elements have obvious grain boundary segregation effect. When the impurity element adsorbed on the grain boundary, the energy of grain boundary is decreased, which reduces the driving force of interface movement and impedes grain boundary movement and limits the growth of grain in solder matrix. On the other hand, the proper amount rare earth elements can significantly improve the microstructure and properties of the solder, but excessive addition will precipitate a large number of rare earth rich phases in the solder, which is easy to be oxidized and lead to the tin whisker problem of solder.
Attempting to study the processing technology on the basis of existing research may change some properties of the alloy [55][56][57], for example, the high performance can be obtained by powder metallurgy technology and the samples extruded at high temperature exhibit better microscopic properties [58]. Figure 6 shows a typical microstructure of as-extruded Sn-0.7Cu alloys [59]. The microstructure obtained by cold extrusion is characterized by finer grains and lower porosity. It seems that the extrusion process promotes profound changes in the microstructural characteristics of solder since the eutectic structure has not been found in the samples. However, the microstructures of cold extruded samples seem to retain some characteristics during atomization, such as dendritic IMC particles with good distribution of Cu 6 Sn 5 IMC ( Figure 6(c,d)), rod-like or fine alveolar, as marked by the arrow, which may lead to mechanical strength related results.
In addition, the rapid and directional solidification solder alloys have finer microstructures with less microsegregation, which ultimately improves the mechanical properties of solder joints [60]. Alternating lamellar eutectic structure and Sn-rich phase were observed in the longitudinal section of directionally solidified hypereutectic Sn-1.0Cu solder, growing in a specific direction, which results in the anisotropic characteristics of the directionally solidified solder because the compressive strength along the longitudinal direction is much higher than that along the transverse direction [61]. The large dynamic supercooling occurring under rapid solidification is the intrinsic mechanism of such a layered structure.
The Cu 6 Sn 5 single fibre spacing and single crystal diameter are mainly controlled by solidification rate during solidification, and both of them decrease with the increase of the solidification rate [62]. In addition, the melt overheating treatment on Sn-Cu solder alloy can obviously refine the solidified microstructure of the alloy, make the interfacial compound layer of the soldering joints thinner, and improve the roughness of the interface. After structural transformation a large number of solid-like clusters are broken, and the clusters which could become the critical nucleus directly disappear or decrease. The smaller clusters can reach the critical nucleation size only at a greater degree of supercooling. With the increase of degree of supercooling, the nucleation rate increases and the critical nucleation radius decreases, which leads to the refinement of solidification structure.

Interfacial reaction
For lead-free solders, the metallurgical reaction between solder and substrate forms IMCs during soldering. IMCs such as Cu 6 Sn 5 and Cu 3 Sn are often formed at the solder/substrate interface in the soldering joints [63]. With aging, IMCs grow at the interface and may be accompanied by the formation of Kirkendall voids. The rapid growth of brittle IMCs and formation of voids at the interface will worsen the performance of soldering joints. Therefore, controlling the thickness of IMCs and voids at the interface can effectively improve the reliability of soldering joints. At present, the researches on inhibition of IMCs at the Sn-Cu lead-free solder interface mainly focus on alloying, particle strengthening, soldering process optimization and substrate and coating material.
It has been reported that the first phase of nucleation and growth at the Sn/Cu interface is Cu 6 Sn 5 . Under the condition that the thickness of the layer is less than several hundred nanometers, the growth of η-Cu 6 Sn 5 will inhibit the nucleation and growth of the second phase ε-Cu 3 Sn [64]. Figure 7 shows the growth pattern of IMCs at the interface between Cu and liquid Sn.
(i) In the oversaturated Sn-Cu liquid alloys, the η-Cu 6 Sn 5 phase nucleate heterogeneously at the liquid/Cu interface and grow continually until a successive thin layer of η-Cu 6 Sn 5 with tens of nanometers thick is formed at the interface. (ii) The rapid diffusion of copper atoms passes through thin and continuous η-Cu 6 Sn 5 boundaries, realizing the rapid growth of individual faceted grains (scallops) of η-Cu 6 Sn 5 phase on a continuous thin layer. (iii) The scallop like Cu 6 Sn 5 grains continue to grow at the interface along with the growth of ε-Cu 3 Sn phase at Cu/η-Cu 6 Sn 5 interface. The influence of Cu content on the interface IMC between Sn-Cu/Cu interface was researched [65]. It was found that the higher the soldering temperature, the thicker the Cu 6 Sn 5 formed. At the same soldering temperature, with the increase of Cu content in the solder, the thickness of IMC layer was decreased and then increased. When the content of Cu is less than 1.1%, a part of Cu 6 Sn 5 grains will dissolve into the solder, resulting in the decrease of IMC. While the content of Cu is higher than 1.1%, the Cu 6 Sn 5 in the solder will deposit and the IMC layer will become thicker. El-Rehim and Zahran [66] investigated the effect of aging treatment at different temperatures on Sn-xCu (x = 1,2,3,4,5%) solder. Comparing the microstructure of Sn-1.0Cu aged at 393K and 433K, it was found that the growth of Cu 6 Sn 5 was coarser at higher temperature. The Cu 6 Sn 5 precipitated first during reflow and then the Cu 3 Sn precipitated after a certain time. The Cu 6 Sn 5 and Cu 3 Sn both grow at the beginning of isothermal heat treatment. After consuming all available Sn, the Cu 3 Sn is formed at Cu/Cu 6 Sn 5 interface at the expense of Cu and Cu 6 Sn 5 . Therefore, the increase of Cu content will make Cu 3 Sn more intensive.
During the long time annealing, the crackle is formed at the interface between Cu substrate and Cu 3 Sn layer, leading to lower reliability of the solder joints. This influence is often caused by Kirkendall voids formed by different diffusion rates of Sn and Cu [67]. It has been confirmed that the addition of alloying elements can affect the growth behaviour of IMCs and the formation of Kirkendall voids [68,69]. Adding a small amount of Ni to Sn-0.7Cu alloy can significantly change the morphology of IMC, inhibit the formation of Cu 3 Sn layer and slow down the dissolution rate of the substrate [70]. Maeshima et al. [71] studied the effect of Ni addition to Cu substrate on the diffusion behavior of Cu and Sn atoms at the interface. Compared with Cu substrate without Ni addition, the addition of Ni effectively inhibited the formation of voids and the growth of Cu 3 Sn layer in the process of mutual diffusion between Cu substrate and Sn-0.7Cu solder. As shown in Figure 8, with the increase of Ni content, the void decreases, and the void rate decreases significantly when the content of Ni reaches 0.2%. In addition, with the increased of Ni content, the thickness of Cu 3 Sn layer decreased and the thickness of Cu 6 Sn 5 layer increased. It was found that the void fraction was positively correlated with the Cu 3 Sn layer and negatively correlated with the Cu 6 Sn 5 layer. Since the total IMC was composed of two  compounds, the maximum thickness of IMC was obtained when the Ni content was 0.09%. The growth of Cu 3 Sn layer at the interface lies on the diffusion flux of Cu and Sn atoms in the substrate and the solder. The experimental results showed that the Ni addition did affect the diffusion flux of Cu and Sn atoms, thus affecting the growth rate of Cu 3 Sn.
The growth of Cu 6 Sn 5 and Cu 3 Sn layer of Sn-0.7Cu solder containing TiO 2 and Ni after isothermal annealing was investigated [72]. With the TiO 2 addition, the scallop-like Cu 6 Sn 5 phase became flatter and the interfacial boundary decreased. After a long time annealing, the Kirkendall voids appeared in the Cu 3 Sn layer, while in the solder joints with the Ni addition, the scallop-like (Cu,Ni) 6 Sn 5 appeared to be finer, and the Cu 3 Sn was thinner, which indicated that Ni inhibited the diffusion of Cu from the substrate to the Cu 6 Sn 5 layer, farther inhibiting the growth of Cu 3 Sn.
Ni element is also commonly used as a barrier layer between the Cu substrate and solder because it can slow down the metallurgical reaction rate during soldering [73,74]. The research of Sn-0.7Cu/Ni interfacial reaction showed that a thin layer of Ni 3 Sn 4 will be formed at the Cu 6 Sn 5 /Ni interface with the continuous growth of Cu 6 Sn 5 layer during soldering, and eventually Ni 3 Sn 4 particles will diffuse into the solder melt. The evolution of this interfacial reaction is mainly influenced by the composition and grain size of solder, especially the Cu content in solder [75]. When the content of Cu increased to 0.4%, the interfacial reaction products changed from Ni 3 Sn 4 to Cu 6 Sn 5 and when the content of Cu was more than 0.6%, the layer of Cu 6 Sn 5 appear peeling phenomenon [76]. The interface between Sn-0.7Cu and Sn-0.4Cu solder at 250°C for 3 min is shown in Figure 9 [77]. The Cu 6 Sn 5 phase of Sn-0.7Cu/Ni has a finer rodlike structure. In addition, the Ni substrate boundaries of Sn-0.7 Cu/Ni solder is straight and irregular for Sn-0.4Cu. As shown by the arrow in Figure 9(b), there are no more products at the concave interface, which reflects that the consumption rate of Ni here is faster, resulting in irregular shape of the substrate. As shown in Figure 9(c), the reaction phase morphology of Sn-0.7Cu-0.1Ni/Ni is similar to that of Sn-0.4Cu/Ni, but the interface is straight since the addition of Ni reduces the dissolution of Ni substrates. The nucleation sites of Cu 6 Sn 5 increase with the increase of Cu content, and the nucleation mechanism is dominant. The morphology of Cu 6 Sn 5 phase transforms into slender rod shape with the low solubility of Ni. In thermodynamics, if the Ni solubility is high, the Cu 6 Sn 5 phase will be stabilized. Adding Ni to the solder contributes to the growth of Cu 6 Sn 5 and hinders its nucleation. The growth mechanism plays a major role, resulting in a small number of large-sized Cu 6 Sn 5 grains. Compared with Sn-0.7Cu/Ni, the interface in Sn-0.4Cu/Ni is obviously coarsened. Because of the low content of Cu, Ni dissolves into Sn-0.4Cu rapidly. At this time, the growth mechanism of Cu 6 Sn 5 phase plays a major role, which also explains the coarsening of Cu 6 Sn 5 phase in Sn-0.7Cu-0.1Ni/Ni. On the other hand, the Ni addition may cause the spalling of solder joint at interface IMC layer, resulting in deterioration of solder joint performance [78,79]. Unlike the preferential substitution of Ni for the Cu atom in Cu 6 Sn 5 , the substitution of the Zn for Sn atom in the sublattice seems to lead to a more stable thermodynamic structure [80]. Zeng et al. [81] investigated the influence of aging on the phase stability of IMCs at the interface of Sn-Cu solder joints containing Ni, Zn and Au. It was found that Ni, Zn and Au inhibited the phase transformation of hexagonal to monoclinic Cu 6 Sn 5 driven by aging, leading to the improvements in phase stability. This discovery helps to further comprehend the reliability of the interface structure of microalloyed lead-free solder joints.
The Al addition can cause significant changes in Sn-0.7Cu/Cu interface structure [69]. The interface IMC is Cu 6 Sn 5 in Sn-0.7Cu-(0.01-0.025)Al solder and Al 2 Cu in Sn-0.7Cu-(0.05-0.075)Al solder, since the low solidification solubility of Al atoms in the matrix of β-Sn and the tendency to segregation in the interface during solidification, which makes the transition of Cu 6 Sn 5 into δ-Al 2 Cu phase. The thickness of scallop-like IMC is mainly controlled by the change of IMC and the reaction between Al and Cu. The effect of (0.05-0.075)Al addition on the thickness of IMC layer is weak. But the thin brittle interfacial IMC is conducive to the bonding strength and reliability of the solder joints [82]. A small amount of Al addition to Sn-0.5Cu solder alloy can contribute significant change of the microstructure too [83]. The Cu-Al IMC with rhombic hexahedral structure was determined by transmission electron microscopy and electron probe microanalysis. The addition of Al in the soldering alloy was beneficial to the formation of Cu-Al IMC in the soldering alloy matrix, named Cu 33 Al 17 , which resulted in the refinement of Cu 6 Sn 5 in the solder alloy. The solder alloy with 0.03%Al exhibited the best properties.
The influence of Sb addition on the interface reaction of Sn-0.7Cu/Cu was investigated [84]. When the content reached 0.5%, the IMC morphology of solder joint interface changed greatly, the scallop IMC was refined and the thickness of IMC layer was the smallest under this condition. As the content increased, the IMC grains coarsened and the thickness of the interface layer increased gradually. It is reported that the addition of microscale Cr can effectively inhibit the growth of Cu-Sn IMC [85,86]. Figure 10 shows that for Sn-3.0Ag-0.5Cu and Sn-0.7Cu solders, the thin Cu 3 Sn IMC layers are formed at the Cu 6 Sn 5 /Cu interface after aging at 150°C for 100h [87]. A similar phenomenon occurs only when the Sn-0.7Cu-0.2Cr solder alloy is aged at 150°C for 500h and the Figure 10. Cross-sectional SEM images of IMC layers after aging at 150°C for up to 1000 h. Reproduced with permission from [87]. thickness of IMC containing Cr seems to be thinnest at any stage. In thermodynamics, the formation of Cu 3 Sn IMCs between Cu 6 Sn 5 IMC layer and Cu is spontaneous, but this can be dominated by kinetic parameters, such as the diffusion of Sn to Cu 6 Sn 5 IMCs or Cu substrate. The authors insisted that Cr inhibited the growth of IMC at solid-state interface by slowing down the diffusion rate of Cu. Unlike Ni atom, the Cr atom can not form the solid solution in CuSn IMC. Many CrSn 2 particles take root at the interface and undergo mature growth during aging. The inhibition behavior may be related to the existence of small particles at the interface and the influence of the flow of Cr and Sn atoms on the diffusion of Cu and the bonding of Sn and Cu atoms.
Among the alloying elements researched, Co is also potential based on its positive influences [88,89]. The effects of minor Co additions on interface reactions of solders/Cu substrate have been investigated in the literature [90][91][92]. The micrographs of Sn-0.7Cu-Co/Ni interfacial reactions with Co additions were shown in Figure 11(a,b) [93].
Compared to the 0.01%Co addition, when the amount of Co addition increased to 0.04%, Ni 3 Sn 4 phase beneath the Cu 6 Sn 5 phase can be observed. Along with Co additions, the thicknesses of the Cu 6 Sn 5 and Ni 3 Sn 4 phases decreased and increased, respectively, and the total thicknesses decreased.
Remarkably, the dissolution of Co in Cu 6 Sn 5 and (Cu, Ni) 6 Sn 5 phases has no effect on the grain morphology but it does refine the grains on either substrate, as shown in Figures 12 and 13 [93]. With Co additions, the more sites for Cu 6 Sn 5 phase nucleation were provided, because the catalysing effect of Co, hence more Cu 6 Sn 5 was refined.
The influencing mechanism of rare earth elements is also a hot topic in the research of lead-free interconnects. The trace amount of Ce (about 0.1%) could inhibit the growth of IMC layer in Sn-Cu solder joints, but adding excessive Ce could promote the growth of IMC layer, which may be caused by the different effects of different amounts of Ce on the diffusion behaviour of Cu at the interface [94]. In addition, with the increase of temperature, the effect  of Ce on interface reaction weakened gradually. Hu et al. [95] investigated the interface reaction of Sn-0.7Cu-xEr/Cu solder joints. It was found that the rare earth element Er inhibited the growth of IMC layer (including Cu 6 Sn 5 and Cu 3 Sn), and the higher the content of Er within tolerable limits, the stronger the inhibition. It depends not only on the concentration gradient of elements but also on the activity of elements. Trace rare earth Er is insoluble in the Sn matrix but has the Sn-affinity to react with Sn, which reduces the activity of Sn and further inhibits the growth of Cu 6 Sn 5 IMC layer. As shown in Figure 14, after isothermal aging, the grain size of IMC layer grows obviously, the morphology of Cu 6 Sn 5 phase becomes flat, the Cu 3 Sn layer thickens sharply and some Kirkendall voids appear at the interface of Cu 3 Sn/Cu. Remarkably, the voids in the joints with 0.5% Er are less than those with 0.1% Er.
The addition of rare earth Pr and Nd can effectively change the morphology of IMC layer in the interface reaction of Sn-0.7Cu-0.05Ni-xPr(Nd)/Cu solder joints [53,54]. As shown in Figure 15, with the addition of 0.05% Pr, the thickness of IMC layer decreases significantly and the formation of voids at the interface is inhibited. Because of the good affinity between Pr and Sn, the two elements are easy to form stable compounds at the interface and prevent the reaction of Sn and other elements to some extent, reducing the activity of Sn at the interface, thus inhibiting the interface reaction of solder/ Cu substrate. On the other hand, PrSn 3 /NdSn 3 formed by Pr/Nd reacting with Sn has the higher melting point, so it will precipitate preferentially during solidification, forming heterogeneous nucleation particles, promoting solidification of solder alloys, shortening the interface reaction time and inhibiting the growth of IMCs.
A part of the minor elements effects on the IMCs based on the current research data of Sn-Cu lead-free solders are provided in Table 2.
The phase field method has been used for the simulation of interfacial reactions. The effects of Figure 13. Grain morphology of the (Cu, Ni, Co) 6 Sn 5 phase formed in Sn-0.7Cu-Co/Ni couples. Reproduced with permission from [93]. grain boundary diffusion coefficient and interfacial energy between primary IMC and liquid Sn on the microstructure evolution and growth kinetics of Cu 6 Sn 5 interface in Sn/Cu interconnection system were researched by using the multiphase field model [96]. It was found that the thickness of IMC was positively correlated with the grain boundary diffusion coefficient and negatively correlated with the interfacial energy, whereas the average transverse grain size of Cu 6 Sn 5 was inversely correlated with them. Combining the 2D and 3D simulation results of IMC morphology evolution at the interface with the experimental results, the simulation results showed good agreement with the experimental results. Ma [97] used a binary alloy phase field model to simulate the formation, morphological evolution and growth of Kirkendall voids in the Cu/Cu 3 Sn interface and IMC layer of Sn/Cu interconnection system. The effects of interfacial Cu 3 Sn layer thickness and impurity content on the morphology and growth kinetics of Kirkendall voids were simulated and analysed. The results showed that a large number of atom mismatch regions can be formed at the Cu/Cu 3 Sn interface, and then grew into Kirkendall voids. With the aging process, the voids grew and merged. In addition, both the number and size of Kirkendall voids were positively correlated with Cu 3 Sn layer thickness and impurity content.

Melting characteristics
The basic thermal properties of eutectic Sn-0.7Cu solder alloy are shown in Table 3 [98]. The melting characteristics of lead-free solders are similar to those of Sn-Pb solders. That is beneficial to follow the existing soldering process and equipment. On the other hand, it is vital to reduce the damage of circuit board components caused by heat output during brazing as far as possible.
Usually, the element doping can affect the melting characteristics of Sn-Cu binary alloy, but the effect seems to be rather weak. For example, the addition of Bi and P can reduce the melting point of Sn-0.7Cu alloy in a small range [99]. After adding 2% Ag and 2% In to the Sn-0.7Cu solder alloy [43], the melting point decreased from 227.4°C to 224.0°C and 217.8°C, respectively, which could be attributable to softening and dissolution of second phase particles. In other words, with Ag and In   addition, the formation of reinforcing IMC phase leads to the increase of surface instability and the transformation in physical properties of the grain boundary/interfacial characteristics. Li et al. [100] considered that the melting point was not significantly affected when the content of In in Sn-0.7Cu-0.2Ni solder was less than 0.3%, but the melting range of the solder increased obviously. The addition of Co in Sn-0.7Cu alloy advances the formation of (Cu,Co) 6 Sn 5 and (Cu,Co)Sn 2 IMCs which seem to play a role in stabilizing microstructure [101], while with the increase of Co content, the melting point of composite solder alloy tends to increase (Sn-0.7Cu-2Co alloy melting point is 232.2°C) [102]. The purpose of adding these components is to maximize the mechanical and other properties of the solder alloy and improve the reliability of lead-free solder joints on the premise of not excessively increasing the melting point of the alloy. This is a worthwhile idea for the modification of lead-free solder. Table 4 shows the peak temperatures for each vertex based on the differential scanning calorimetry (DSC) data of three solder alloys. The addition of Ti can effectively reduce the undercooling of solder, thus changing the solidification behavior and microstructures of solder alloys [103].
Adding TiO 2 nano-particles to Sn-0.7Cu solder alloy can slightly improve the melting properties. With the increase of the content of TiO 2 , the solidus and liquidus temperatures and melting range of the alloy decrease slightly, which may be due to the increase of the surfacefree energy of the solder alloy caused by the TiO 2 particles addition. Moreover, the properties of TiO 2 /interface at the grain boundaries of the solder were changed significantly, which resulted in the change of the physical properties [50]. Table 5 provides a summary of the alloy composition and the data of melting points based on the current research of Sn-Cu lead-free solder.
A large number of researches have shown that the effect of the element addition on the melting point of Sn-Cu solder alloy seems not to be remarkable, but the refinement of solder microstructure and the strengthening of other properties by element doping could not be neglected. To solve the problem of excessive melting point of Sn-Cu solder, the research can start with the solder alloy itself or the melting range of the solder which could be shorten by optimizing the soldering parameters, such as the rapid solidification technology [104,105] and directional solidification technology [106]. The spreading and melting of the solder can be realized in a short time, reducing the heat release and the thermal damage of the electronic components during the soldering process. In addition, it has been reported that the atomization and extrusion of solder alloy can improve the melting properties and other mechanical properties of solder alloy [107].

Wettability
Wettability refers to the ability of a liquid metal to wet and spread on the parent metal surface. It can also be described as the trend of liquid spreading on solid substrates [108]. Wettability is determined by the surface and interfacial energy involved in the solid/liquid interface, which is influenced by many factors, such as liquid viscosity, interfacial reaction and thermal conditions of the system [109]. Several important indicators of wettability evaluation include the contact angle, wetting force, wetting time. The wetting and spreading of solder on the surface of solid base metal are mainly caused by the different interfacial tension between solid and liquid and the surface tension of liquid. After the spreading and wetting of droplets on the solid plane interface, it will eventually reach equilibrium state, that is, the surface tension at the three-phase boundary points of the system will reach equilibrium. This state can be described by Young's equation: where σ SG is the surface tension acting on droplets along boundary between solid and gas, σ SL the surface stress on solid-liquid boundary, σ LG the surface tension of liquid on the boundary of gas medium and θ the wetting angle in equilibrium state.   In the actual soldering process, there will be violent interaction between base metal and solder. In this case, the surface wetting, spreading and capillary phenomena are more complex, so the above equation is only an approximate description. Table 6 describes the natural radius of curvature, R, of the alloys, calculated by Equation (2). Compared with Sn-40Pb, Sn-0.7Cu solder alloy has a larger natural curvature radius. The implication of this result is that the phenomenon of bridging must be given special attention, along with the trend of decreasing solder joint spacing.
where γ is the surface tension, ρ the density and g the acceleration due to gravity. During soldering, the viscosity of solder alloy directly affects gap filling and weldability. The viscosity of Sn-0.7Cu solder alloy decreases with the increase of temperature [110]. But with the increase of temperature, the liquid structure of the melt could be changed, and the surface tension of the solder first decreases to a certain value and then increases slightly. If only the wettability of solder is considered, the optimum soldering temperature for Sn-0.7Cu alloy is 303°C, under which the minimum surface tension is about 369 mN/m [22]. The surface tension of Sn-based binary lead-free solder alloy can be calculated and its wettability can be evaluated by melt viscosity value based on the expression of surface tension and viscosity [111]. The relationship between surface tension and viscosity in monolithic system and vacuum is deduced as follows: Where γ is the surface tension, η is the viscosity, k is the Boltzmann constant, T is the absolute temperature, and m is the atomic mass. In addition, the viscosity of the melt is approximately expressed by the following equation [112]: where h is Planck's constant, v m is the flow unit volume and ε is the activation energy to move the flow unit in the melt.
As shown in Figure 16 [110], the surface tension of liquid Sn-Cu solders at different temperatures was calculated, based on the above two formulas. The surface tension of the two kinds of solder is similar. The smallest values were obtained at 633 K for Sn-2Cu and 603 K for Sn-0.7Cu, respectively.
It is a practical and effective method to study the influence of element doping on the wettability of solder under laboratory conditions. Huang et al. [113] researched the effect of S element on the wettability of Sn-0.7Cu solder on Cu substrate in 3.5% NaCl solution. Figure 17 shows that the wetting performance of Sn-0.7Cu solder can be greatly improved by adding 0.08% S. S is easy to concentrate on the surface of the solder melt during the soldering process, which reduces the surface tension of the alloy since the non-metallic element S is difficult to dissolve into the alloy. In addition, the addition of S inhibits the oxidation of Sn. These two mechanisms promote the spreading of solder melt on the Cu substrate. On the other hand, the formation of SnS and SnSO 4 by the addition of excess S hinders the flow of solder melt and cancels the positive effect.
The effect of Ni content on the wettability of Sn-Cu-xNi solder on Cu substrate was investigated by Silva et al. [114]. It was found that Sn-0.7Cu solder with 0.05%Ni had smaller wetting angle, and the relationship between initial contact angle and heat transfer coefficient was revealed. In addition, with 0.3% In addition to the Sn-0.7Cu-0.2Ni soldering alloy, the optimum thermal expansion coefficient of the soldering alloy was 17.5 × 10 −6 /°C. The spreading area of the soldering alloy increase by 15.6% with the Figure 16. Surface tension of liquid Sn-Cu solders. Reproduced with permission from [110]. increase of thermal expansion coefficient [99]. The contact angles of Sn-0.7Cu-0.3Ni and Sn-0.7Cu solder under different conditions are shown in Figures 18 and 19 [111]. The lower contact angles with Cu substrate for both solder is found by using no-clean (NC) flux. Analogously, the lower contact angles with Ni substrate for both solder is found by using water-soluble (WS) flux. It seems that the nonactivated (R) flux is not suitable for both solder, especially on Ni substrate. In addition, with the rise of solder bath temperatures, both the contact angle of Sn-0.7Cu and Sn-0.7Cu-0.3Ni solder decreases. Moreover, with the addition of 0.3Ni into the Sn-Cu solder shows better wettability.
Zhu et al. [45] researched the influence of Zn particles on the wettability of Sn-0.7Cu solder. With the increase of Zn particles, the spreading coefficient of the solder decreased first and then increased. With the addition of 0.2% Zn particles, the spreading coefficient was the largest (79.43%). When the addition is more than 0.2%, the spreading coefficient of the solder decreased, which is due to the addition of trace Zn particles increase the effective amount of heterogeneous nucleation on the substrate and promote the growth of interfacial IMC. The appropriate thickness of interfacial IMC layer is helpful to the flow of the solder melt on the Cu substrate, thus improving the spreading performance. However, the excessive Zn particles could produce agglomeration phenomenon and float on the surface of the solder melt, which increased the viscosity of the solder melt and reduces its fluidity, thus showing a poorer spreading performance.
With the increase of Al concentration, the spreading coefficient of Sn-Cu-Al solder increases. Figure 20 shows the relationship between Al content and the diffusion coefficient of Sn-Cu-Al solder alloy on the Cu substrate [39]. When the Al content reaches   0.075%, the diffusion coefficient of the solder alloy increases to about 70% from the initial value of 65.23%. It is evident that the addition of Al promotes the wetting of solder alloys, which attributes to the decrease of surface tension of liquid solders due to the high activity of Al element. In addition, the metallurgical reaction of forming Al 2 Cu phase consumes part of the Cu from the substrate, thus promoting the spread of solder [40].
The effects of Cr, Ca and Pd on the wettability of Sn-Cu/Cu were investigated [85]. Typical contact angles of several reflowed samples on Cu substrates are shown in Figure 21. The results of the wetting angles show that Cr and Ca enhance the wettability of Sn0.7Cu solder alloy. Similar to Al element, the addition of Cr element can produce many thin rod-like CrSn 2 IMC at the interface, resulting in lower surface tension. While the Ca addition can refine eutectic phase at the grain boundary, making rod-like IMC thinner near the interface, which is conducive to the spread of solder melt on the substrate.
It is noted that the wetting behaviour of Sn-Cu lead-free solder is affected significantly by the substrate material, temperature and flux. As shown in Table 7, the wetting behaviour of Sn-Cu lead-free solders by a part of the alloying elements reported is summarized.
A large number of studies have shown that the wetting in the actual soldering process is related to the properties of the solder, but mainly depends on the role of the soldering fluxes [115][116][117]. Moreover, the influence of different kinds of flux on the wettability of solder is significant, for example, the differences in contact angles for Sn-0.7Cu and Sn-0.7Cu-0.3Ni solders by three different fluxes [111]. Under atmospheric conditions, the surface of the solder metal and substrate metal will be covered with a layer of the oxide film, which is very unfavourable to the spread of the solder melt on the substrate metal. In the soldering process, the use of fluxes can remove the oxides on the surface of the solder and substrate metal well, creating good conditions for the solder to infiltrate in the substrate metal. In addition, the flux can cover the substrate metal and the solder surface with a thin liquid layer to avoid the occurrence of secondary oxidation. Finally, it can enhance

Mechanical properties and creep
The mechanical behaviour of solder is vital to the strength of the solder joints. Although the solder volume, joint geometry, bonding process and solidification rate have different effects on mechanical properties, the most essential factor is the alloy composition of solder. The effects of different element doping on the mechanical properties of Sn-Cu solder alloys were discussed, including tensile shear properties, hardness values and creep properties. The ultimate tensile strength (UTS) of Sn-0.7Cu solder alloy is about 30 MPa at room temperature [52]. Hung et al. [31] found that when the Cu content of Sn-xCu solder increased, the Cu-Sn IMC increased and the Sn-rich phase refined. For the samples with low Cu content (0.3Cu and 0.6Cu), they have the good mechanical properties and long fatigue life due to the layered deformation structure of Sn-rich phase. The brittle and hard Cu 6 Sn 5 phase can reduce the mechanical properties of solder joints, but when the Cu content reaches more than 1.3%, the grains are refined and the Cu 6 Sn 5 phases are dispersed which must be one reason that the deformation resistance of Sn-rich phase strengthened and the stress-centralized effect of the Cu 6 Sn 5 phase decreased.
The mechanical properties of Sn-0.7Cu(Ni) solder alloy exhibit strong temperature dependence and strain rate sensitivity in tensile tests at different temperatures and strain rates [118]. Figure 22 shows that yield strength (YS) of Sn0.7Cu(Ni) is smaller than that of Sn-37Pb, and both decrease with the increase of temperature. Alam et al. [57] added different amounts of nano-Cu particles in Sn by microwave sintering assisted powder metallurgy route to obtain compact materials with nearly equiaxed grains. Tensile test results show that, compared with Sn-0.7%Cu solder, adding 0.35vol.% (0.43wt.%) Cu in pure Sn can significantly improve the YS of solder alloys to 233% and UTS to 159%. The main feature of this preparation method is its cost-effectiveness.
The mechanical properties of the Sn-Cu lead-free solder alloy were improved, similar to the traditional Sn-Pb solder, by adding the trace alloying elements to the alloy. The mechanical properties of Sn-Cu solder are significantly affected by the addition of Al [39,40]. The UTS of the Sn-Cu-(0.01~0.025)Al solder alloy was deteriorated by the coarsened Cu 6 Sn 5 /Sn interface. The microstructure of Sn-Cu solder is refined by micro Al addition, but the tensile strength of Sn-Cu decreases with the increase of volume fraction of the brittle phase. With the increase of Al content (0.05~0.075), the formation of Cu 6 Sn 5 IMC was inhibited. The precipitated fine Al 2 Cu acted as strengthening phase, which hindered the movement of tensile dislocation, and was beneficial to the improvement of UTS of solder joint. On the other hand, the UTS of Sn-Cu-Al solder is related to the distribution and strength of precipitated phases. The microhardness values of Al 2 Cu/Sn eutectic and β-Sn are 76.3 MPa and 11.7 MPa, respectively. The improvement of UTS of Sn-Cu-Al solder alloy is the result of the refinement structure of Sn-Cu-0.075Al alloy and the interaction of Al 2 Cu/Sn eutectic with high microhardness. Hasnine M and Vahora N [119] added 0.01% Ge to Sn-0.7Cu solder alloy. The results Figure 22. The ultimate tensile strength of two solder alloys Sn37Pb and Sn0.7Cu(Ni) in the temperature range from −25°C to 125°C (with a constant strain rate of 1.17 × 10 −3 S −1 ). Reproduced with permission from [118]. showed that the microhardness of as-cast alloy increased by 6.7%, which was attributed to the refinement of grain structure and the uniform distribution of IMC in eutectic phase caused by the addition of Ge.
The experimental results of mechanical tests of Sn-Cu solder alloy with Ag and In addition is shown in Figure 23 [44]. The Sn-0.7Cu-2Ag-2In solder alloys exhibit the highest tensile strength 47.3 MPa, which is approximately 1.7, 1.3 and 1.2 times that of Sn-0.7Cu, Sn-0.7Cu-2In and Sn-0.7Cu-2Ag alloys, respectively. Also, for the same strain rate, the YS of Sn0.7Cu-Ag-In alloy has highest value 38.2 MPa, among the four solders investigated. It is obvious that the Ag and In addition can enhance the tensile/shear properties of solder, which can be attributable to the strengthening mechanism of IMC phases such as Ag 3 Sn, InSn 4 and In 4 Ag 9 in the alloy matrix.
The growth of the interfacial layer of solder joints can be effectively inhibited by adding alloy elements or compound particles into the solder. The tensile properties of Sn-0.7Cu solder could be significantly improved by adding nano-TiO 2 particles to the solder. When the content of nanoparticles was 1%, the UTS increased by 33.4%, and the yield limit of alloy increased by 43% [50]. As shown in Figure 24, the Ni and nano-TiO 2 particles addition could increase the shear stress of Sn-0.7Cu solder joints to varying degrees, and the slope of the shear stress curves of Sn0.7Cu and Sn0.7Cu-TiO 2 as reflowed are also reduced, which indicates the better fracture characteristics [72]. With 1% TiO 2 addition, the average shear strength of Sn0.7Cu solder joint was increased by about 20% while the addition of 0.05% Ni increased that by about 28%. This strengthening effect may be attributed to the inhibition of Cu 3 Sn IMC layer by nanoparticles and the positioning of dislocations in the solder matrix. In addition, the tensile properties of Sn-0.7Cu solder joints could be improved by adding micron-sized Zn particles [45]. When the content of Zn particles was 0.2%, the UTS of composite solder joints was 41.26MPa which was increased by nearly 20%. Zn particles could make fine Cu 6 Sn 5 particles disperse on the β-Sn matrix and play a role of dispersion strengthening, hindering the dislocation movement in the tensile process, thus improving the tensile properties of composite solder joints. However, excessive particle addition will cause the coarsening of IMC and stress concentration, resulting in crack initiation and propagation during the tensile process. Sn-0.7Cu lead-free composite solders with different content of Si 3 N 4 were prepared by powder metallurgy [120]. The effects of different content of Si 3 N 4 particles on the melting point temperature, hardness, shear strength and surface fracture mechanism of the solder was investigated. The results showed that when the content of Si 3 N 4 particles exceeds 1%, the strength performance of the solder joint rose significantly.
The solid solution strengthening of rare earth atoms, the grain refinement and stress concentration along the irregular shape of rare earth particles are considered to be the main factors affecting the mechanical properties of solder alloys. A number of experiments showed that the mechanical properties of lead-free solder joints can be improved by about 12% with the addition of rare earth elements (Ce, Y, La, Er), while the mechanical properties of lead-free solder joints can be improved by nearly 25% with the addition of Pr and Nd, which may be related to the distribution of Pr and Nd elements outside the arrangement of extranuclear electrons [54]. Zeng et al. [121] considered that the tensile strength of solder joints could be improved to the greatest extent when the content of Nd in Sn-0.7Cu-0.05Ni solder reached 0.05%. The addition of Nd changed the morphology of the IMC layer and made it flatter. In addition, the addition of Nd reduced the activity of Sn at the interface, inhibited the excessive growth of IMC layer at the interface, and reduced the spalling tendency of IMC layer at the solder joint interface. As  shown in Figure 25, with 0.25% and 0.5% RE addition, the UTS of Sn-0.7Cu composite solder is increased by 20% and 27%, respectively [52]. On the other hand, the elongation of Sn-0.7Cu composite solder shows a decline under normal conditions.
With the development trend of miniaturization of electronic products, the phenomenon of thermal transfer (TM) accompanied with electromigration has become one of the important factors affecting the reliability of solder joints in electronic packaging [63,122]. The accumulation and dissolution of interfacial IMCs are significantly different at both cold and hot ends due to the existence of the temperature gradient, thus affecting the mechanical properties of the solder joints. The mean microhardness of pure Sn and Sn0.7Cu solder is shown in Figure 26 [123]. Both pure Sn and Sn0.7Cu solder exhibited lower microhardness under the action of the temperature gradient. The hardness increases at a relatively constant rate from the hot end to the cold end, which means that the mechanical damage of the hot end is greater than that of the cold end. This may be due to the grain coarsening and the increase of vacancy concentration caused by high temperature at the hot end, leading to the decrease of microhardness.
Creep is the tendency of the slow permanent movement or deformation of solid materials under the influence of stress. The rate of deformation is related to material properties, loading time, loading temperature and structural stress. For some low melting point metals such as Pb and Sn, creep could occur at room temperature. The creep behaviour in Sn-Cu lead-free solder alloy is still easy to occur during service since its melting point [124]. Dislocation climbing and grain boundary sliding are the main mechanisms of creep.
The stress-time relationship Sn-Cu-xAl solder alloy is shown in Figure 27 [69]. It can be seen that the addition of Al does not improve the creep properties of Sn-Cu alloy. The creep resistance of the alloy is guaranteed by the dislocation movement hindered by the dispersed phase. Dislocations are rearranged or annihilated in the combination of positive and negative dislocations. In the dispersion-strengthened alloys cross-slip and multiple slip occur at grain boundaries due to the effect of precipitation relative dislocation motion can reduce the creep rate. However, under the condition of grain boundary precipitation, the creep resistance of the alloy will be reduced in the poor region of the grain boundary. For Sn-Cu-Al solder alloys, Cu 6 Sn 5 and Al 2 Cu are precipitated at grain boundaries due to the metallurgical reaction between Al and Cu, and the formation of IMC layer with continuous brittle interface promotes the formation of dilution zone. The results show that the creep resistance of Sn-Cu-A alloy is reduced by the IMC layer at the brittle interface.
After adding 2% Ag and 2% In to Sn-0.7Cu solder alloy [43], the creep rate of the solder alloy decreased by 521.0% and 200.7%, respectively. The addition of Ag and In not only resulted in the formation of intermetallic compounds Ag 3 Sn and γ-SnIn 4 , but also refined the size of β-Sn from 0.5 μm to 0.15 μm. The creep